The Al-Zn-Mg-Cu alloy strip can be successfully fabricated by twin roll casting. In order to determine the effect of thickness reduction and heat treatment temperature on the recrystallization behavior, the strips were rolled and subsequently heat treated under various conditions. As a result, a fine grained microstructure （average grain size -13 μm, average grain aspect ratio -1.7） and high mechanical properties （UTS ≥360 MPa, δ ≥20%） were obtained by cold rolling with thickness reduction of 60% and heat treatment at 500 ℃ for 1 h. Also, the effect of the microstructure on mechanical properties of the Al-Zn-Mg-Cu alloy strip was discussed. Consequently, the low cost and high strength Al-Zn-Mg-Cu alloy sheet can be fabricated by twin roll casting by proper thermo-mechanical processes.
将双辊铸轧运用于制造Al-Zn-Mg-Cu合金带材。研究带材减薄率及热处理温度对合金再结晶行为的影响。结果表明:在冷轧率为60%、热处理制度为500°C的条件下处理1 h时,合金带材具有细晶组织(平均晶粒尺寸约为13μm,晶粒纵横比约为1.7)和高的力学性能(UTS≥360 MPa,δ≥20%)。研究了微观组织对Al-Zn-Mg-Cu合金带材力学性能的影响。合适的双棍铸轧热处理及加工工艺能制造低价、高强的Al-Zn-Mg-Cu合金带材。
基金
supported by a grant from the Korea Institute of Materials Science (Project No. PNK 3250)
作者简介
Hyotmg-Wook KIM; Tel： ＋82-55-2803307; Fax： ＋82-55-2803599; E-mail： hwkim@kims.re.kr