摘要
水泥土中掺入玄武岩纤维,在不同的水泥含量(10%、15%、20%、25%)条件下,选取5种长度(6 mm、12 mm、18 mm、24 mm、30 mm)和4种掺量(0.3%、0.5%、0.7%、1.0%)作为变量,制作不同龄期的立方体试块(7 d、14 d、28 d),进行无侧限抗压试验和劈裂抗拉试验,研究玄武岩纤维掺入水泥土后对水泥土抗压强度和抗拉强度的影响效果,最终确定了玄武岩的较优掺入长度为18 mm,最优掺量范围为0.5%~0.7%。结果表明,玄武岩纤维对水泥土抗压抗拉强度均有所提升。
In order to test the effects of basalt fiber on mechanical properties of cement soil,the cement soil mixed with basalt fiber with five sizes（ 6 mm,12 mm,18 mm,24 mm,30 mm） and four dosages（ 0. 3%,0. 5%,0.7%,1%） at different cement content（ 10%,15%,20%,25%） was made and tested at different ages（ 7 d,14 d,28 d）. Unconfined compression test and splitting tensile test were conducted to study the effect of basalt fiber incorporation into cement soil on compressive strength and tensile strength of cement soil. The results shows that the optimal incorporation length of basalt is 18 mm,and the optimal dosage range is 0. 5% ~ 0. 7%. The results show that the compressive and tensile strength of the cement soil can be improved by basalt fiber.
出处
《水利与建筑工程学报》
2017年第6期138-142,共5页
Journal of Water Resources and Architectural Engineering
基金
河北省教育厅科研项目(ZC2016161)
张家口科技局科研项目(1611068A)
河北建筑工程学院科学技术研究基金项目(QN201408)
关键词
铁路路基
力学性能
试验研究
玄武岩纤维
railway subgrade
mechanical properties
experimental research
basalt fiber
作者简介
胡建林（1986-），男，河北张家口人，讲师，主要从事地基处理、基坑工程等方面的研究工作。E—mail：hjl185@126．com;通讯作者：杨鑫（1993-），男，河北张家口人，硕士研究生，研究方向为地基处理。E-mail：838470772@qq．com