对玻璃钢/钢结构连接界面粘结强度进行研究,采用不同种类及比例的添加剂对粘结剂-环氧树脂进行改性,并用不同的工艺制作了系列粘结结构试件。根据试验结果,得到了不同试件的拉伸破坏强度和三种典型破坏模式,并对破坏机理进行了分析。
The strength of tensile failure mechanisms of interface for GFRP/steel compounded structures was studied. The adhesive and epoxy was modified by different additive, and the structure specimen were made by different technics. According to experimental results, the strength of structure＇ s tensile failure was found and three kinds of typical tensile failure modes were built up, then the failure mechanism was analyzed.