摘要
目的提高体积微成形件的成形质量。方法利用等径角挤压工艺,沿BC路径对T2紫铜试样进行了8个道次的挤压,获得了延伸率高达56.7%的细晶材料。选择DEFORM软件对微小齿轮的成形过程进行了有限元分析,得到了合适的成形工艺参数。结果利用不同组织的材料,成形出了最小模数为0.1 mm,分度圆直径为1 mm的微小齿轮件。结论实验结果表明,与常规多晶材料相比,细晶材料成形的微小齿轮的尺寸精度有了较大提高。
ABSTRACT:To increase the forming property of micro massive forming parts,fine-grained T2 copper with an elongation of 56.7%was fabricated by using equal channel angular pressing,and the samples were extruded for 8 passes in BC path. The forming process of the micro gear was simulated by using the DEFORM software,and the proper forming parameters were obtained. Micro gears with a minimum modulus of 0.1 mm,and pitch circle diameter of 1 mm were well formed with different materials. The results show that the filling quality and dimensional accuracy was increased by using fine-grained material compared with conventional polycrystalline material.
出处
《精密成形工程》
2016年第3期30-33,51,共5页
Journal of Netshape Forming Engineering
关键词
体积微成形
等径角挤压
细晶T2紫铜
微齿轮
micro massive forming
equal channel angular pressing
fine-grained T2 copper
micro gear