为探究冷却方式对热浸镀锌丝缠绕性能和镀层防腐性能的影响问题,本文讨论了热镀锌镀层的形成过程以及水冷方式对镀层的影响,试验分别采用了缠绕试验、金相分析、盐雾试验等方式,研究了不同的冷却方式对热镀锌丝缠绕性能和防腐性能的影响。结果表明:在生产工艺及水流量一定的条件下,采用环形冷却的方法可以有效控制锌铁合金层厚度从而提高热镀锌丝成品的缠绕性能和整体防腐性能。
In order to explore the influence of cooling methods on the winding properties and anti-corrosion properties of hot-dip galvanized wires,the formation process of hot-dip galvanized wire and the influence of water cooling methods on the coating were discussed.The results show that under the condition of production process and water flow,the annular cooling method can effectively control the thickness of the zinc-iron alloy layer,so as to improve the winding performance and overall anti-corrosion performance of the hot-dip galvanized wire.
作者
于喜彬
王钺涵
李加革
程慧鹏
刘滨源
孙国庆
王新国
孙永鑫
Yu Xibin;WangYuehan;Li Jiage;Cheng Huipeng;Liu Binyuan;Sun Guoqing;Wang Xinguo;Sun Yongxin(Tianjin Huayuan Wire Products Co.,Ltd.,Tianjin 301636,China;China Surface Engineering Association,Beijing 100120,China;Jiangsu Hongli Intelligent Equipment Co.,Ltd.,Yancheng 224001,China)
出处
《电镀与精饰》
北大核心
2025年第6期107-112,共6页
Plating & Finishing
关键词
热镀锌
冷却方式
缠绕性能
防腐性能
hot-dip galvanizing
cooling method
winding performance
anti-corrosion performance
作者简介
通信作者:于喜彬(1965-),本科,高级工程师,高级经济师,研究方向为先进金属材料涂镀、表面处理、新产品研发等,email:yuxibin1965@126.com。