基于Fe-Zn二元相图和典型热浸镀锌层组织,论述了热浸镀锌层的相组成、相结构及其形成过程。利用Zn原子浓度和时间的关系,建立了热浸镀锌层的生长动力学模型,重点讨论了ζ相层的生长动力学,给出了镀层厚度与时间,以及镀层生长速率与扩散系数和浓度梯度的关系;并指出了该领域今后的研究方向。
The phase composition, phase structure and their forming processes of hot-dip galvanizing coating were discussed based on Fe-Zn binary phase diagram and typical microstmcmre of hot dip galvanizing coating. The growth kinetics model of hot-dip galvanizing coating was established using the relationship between Zn atomic concentration and time. The growth kinetics of ~ phase was analyzed in detail. The relationship between the coating depth and time, as well as the relation among the growth rate, diffusion coefficient and concentration gradient were given. The research trends for this field were forecasted.
出处
《热加工工艺》
CSCD
北大核心
2012年第20期122-125,共4页
Hot Working Technology
基金
陕西省科技统筹创新工程计划资助项目(2011KTDZ01-03-06)
汉中锌业有限责任公司科研基金资助项目(HZXY2011003)
关键词
钢材
热浸镀锌
组织
相结构
形成机制
steel
hot-dip galvanizing
microstructure
phase structure
forming mechanism
作者简介
邵大伟(1986-),男,河南西平人,硕士研究生,电话:0916-2291079;通讯作者:贺志荣(1960-),男,陕西乾县人,教授,博士,研究方向为材料热处理、形状记忆合金,电话:0916-2291079,E-mail:hezhirong01@163.com.