摘要
针对全棉贡缎提花面料生产时能耗高、水耗大的问题,采用冷轧堆工艺对其进行前处理和染色,优化了冷轧堆工艺条件。结果表明:冷轧堆前处理后织物白度达到86%,毛细效应达到12.3 cm/30 min,冷轧堆染色织物的染色效果与高温染色效果基本一致。经生产统计,每万米全棉贡缎提花染色面料采用冷轧堆工艺较传统高温工艺能耗降低30%,水耗降低35%,节能减排效果显著。
In order to solve the problems of high energy consumption and large water consumption during cotton satin jacquard fabric production,the cold pad-batch process was adopted for its pretreatment and dyeing,and the process conditions were optimized.The result indicates that the fabric whiteness under the pretreatment of cold pad-batch process reaches 86%,with a capillary effect of 12.3 cm/30 min.The dyeing effect of fabric treated by cold pad-batch process is basically the same as that of high-temperature dyeing.According to production statistics,compared with traditional high-temperature process,the energy consumption for 10,000 meters of dyed cotton satin jacquard fabrics through the cold pad-batch process is reduced by 30%and water consumption is reduced by 35%,and the effect of energy saving and emission reduction is significant.
作者
徐华君
陈万明
王力
张永高
史元庆
章金芳
XU Huajun;CHEN Wanming;WANG Li;ZHANG Yonggao;SHI Yuanqing;ZHANG Jinfang(Zhejiang Haoyu Technology Co.,Ltd.,Shaoxing 312369,China)
出处
《现代纺织技术》
北大核心
2022年第3期179-185,共7页
Advanced Textile Technology
基金
中国博士后科学基金项目(2021M690599)。
关键词
全棉贡缎提花
冷轧堆前处理
白度
冷轧堆染色
K/S值
cotton satin jacquard fabric
cold pad-batch pretreatment
whiteness
cold pad-batch dyeing
K/S value
作者简介
徐华君(1974-),男,浙江上虞人,工程师,主要从事印染技术和生产管理方面的研究;通信作者:章金芳,E-mail:jinfang@zhejianghaoyu.com。