摘要
In this work,La_(2)NiO_(4+δ)-Ce_(0.55)La_(0.45)O_(2−δ)(denoted as LNO-xLDC)with various LDC contents(x=0,10,20,30,and 40 wt%)were prepared and evaluated as bifunctional oxygen electrodes for reversible solid oxide cells(RSOCs).Compared with the pure LNO,the optimum composition of LNO-30LDC exhibited the lowest polarization resistance(Rp)of 0.53 and 0.12Ω·cm^(2)in air at 650 and 750℃,respectively.The enhanced electrochemical performance of LNO-30LDC oxygen electrode was mainly attributed to the extended triple phase boundary and more oxygen ionic transfer channels.The hydrogen electrode supported single cell with LNO-30LDC oxygen electrode displayed peak power densities of 276,401,and 521 mW·cm^(−2)at 700,750,and 800℃,respectively.Moreover,the electrolysis current density of the single cell demonstrated 526.39 mA·cm^(−2) under 1.5 V at 800℃,and the corresponding hydrogen production rate was 220.03 mL·cm^(−2)·h^(−1).The encouraging results indicated that LNO-30LDC was a promising bifunctional oxygen electrode material for RSOCs.
基金
Science and Technology Project of Jiangxi Provincial Education Department(GJJ190734)
The National Natural Science Foundation of China(51962015)。
作者简介
Corresponding author:Pengzhang Li,E-mail:15b911005@hit.edu.cn。