Nanosized SSZ-13 zeolite was synthesized by traditional hydrothermal method using N,N,N-trimethyl-1-adamantanaminium hydroxide as the structure-directing agent (SDA). The influence of different preparative conditions of nanosized SSZ-13 was investigated systematically. The synthetic zeolites were characterized by X-ray powder diffraction (XRD), nitrogen physisorption, and scanning electron microscopy (SEM). By means of the self-assembled method, the thin SSZ-13/polyvinyl alcohol nanocomposite membranes were obtained by incorporating the nanosized SSZ-13 zeolite into the polymeric precursor (polyvinyl alcohol (PVA)). The permeation properties of pure CO2 and CH4 through the mixed matrix membranes (MMMs) were measured. The results showed that the highly crystalline SSZ-13 zeolite in a dispersed nanocrystal form with a controllable particle size of 100 nm could be hydrothermally synthesized by optimizing the synthetic parameters and the selectivity of CO2/CH4 of the MMMs could reach a value of 40 by changing the amount of nanosized SSZ-13 zeolite.
Nanosized SSZ-13 zeolite was synthesized by traditional hydrothermal method using N,N,N-trimethyl-l-adamantanaminium hydroxide as the structure-directing agent（SDA）.The influence of different preparative conditions of nanosized SSZ-13 was investigated systematically.The synthetic zeolites were characterized by X-ray powder diffraction（XRD）,nitrogen physisorption,and scanning electron microscopy（SEM）.By means of the self-assembled method,the thin SSZ-1 3/polyvinyl alcohol nanocomposite membranes were obtained by incorporating the nanosized SSZ-1 3 zeolite into the polymeric precursor（polyvinyl alcohol（PVA））.The permeation properties of pure CO2 and CH4 through the mixed matrix membranes（MMMs）were measured.The results showed that the highly crystalline SSZ-13 zeolite in a dispersed nanocrystal form with a controllable particle size of 100 nm could be hydrothermally synthesized by optimizing the synthetic parameters and the selectivity of CO2/CH4 of the MMMs could reach a value of 40 by changing the amount of nanosized SSZ-13 zeolite.
作者简介
Prof. Luo Yibin, Telephone:+86-10- 82368237;E-mail: luoyibin.ripp@sinopec.com.