摘要
采用压力诱导流动成型(PIF)方法来调控聚苯硫醚(PPS)/玻璃纤维(GF)/碳纤维(CF)三元复合材料的本体结构。并对三元复合材料进行了傅立叶红外光谱分析(FT-IR)、形貌观察(SEM)、力学性能测试、动态力学测试(DMA)和DSC测试,考察了PIF成型的效果。结果表明,在该三元体系中,当CF的质量分数为0.5%时,PIF成型后的复合材料性能最佳,拉伸强度达到362.33 MPa,弯曲强度达到408.11 MPa,冲击强度达到14.35kJ/m^2。
Pressure-induced flow-forming(PIF)was used to control the bulk structure of PPS/GF/CF composites.The ternary composites were characterized by Fourier transform infrared spectroscopy(FT-IR),morphology observation(SEM),mechanical property test,dynamic mechanical test(DMA)and DSC respectively.The results show that when the mass fraction of CF is 0.5%,the properties of PIF composites are the best,and the tensile strength is 362.33 MPa,and the flexural strength is 408.11 MPa and the impact strength is 14.35 kJ/m2.
作者
周志纯
赵丹萍
于跃
郭静
张森
Zhou Zhichun;Zhao Danping;Yu Yue;Guo Jing;Zhang Sen(School of Textile and Material,Dalian Polytechnic University,Dalian,Liaoning,116034;ACRE Coking&Refractory Engineering Consulting Corporation,MCC,Dalian,Liaoning,116085)
出处
《现代塑料加工应用》
CAS
北大核心
2018年第2期28-31,共4页
Modern Plastics Processing and Applications
基金
国家自然科学基金(51403028)
辽宁省自然科学基金(20170540077)
关键词
压力诱导流动
聚苯硫醚
碳纤维
本体结构
pressure-induced flow
polyphenylene sulfide
carbon fiber
bulk structure
作者简介
周志纯,在读硕士研究生,主要从事高分子材料改性与成型加工研究。E-mail:912988047@qq.com。;通信联系人,张森,E-mail:20430155@qq.com。