摘要
以酸洗处理后的南方地区煤矸石及氧化铝为原料,研究了不同试验条件下合成莫来石物相的影响。结果表明:1 200℃开始有棒状莫来石晶体的生成,1 500℃以后莫来石大量生成,温度升高到1 600℃莫来石进一步生成;改变最高温度下的保温时间,莫来石化程度呈现先增后减的趋势;改变煤矸石的用量,随着煤矸石用量的增加,物相中刚玉峰增强,说明煤矸石用量的增加不利于莫来石的合成;改变配料中的铝硅比,由3∶2降低到1∶1过程中,莫来石化程度逐渐加强,在铝硅比1∶1时物相中刚玉峰消失,说明低品位煤矸石在较低的铝硅比下有利于莫来石的合成。
Using the coal gangue after acid leaching and alumina oxide as raw material, the effect of syn- thetic on mullite phase was researched under different experimental conditions. When the heating tempera- ture is 1 200 ℃ a rod like mullite crystal appears,. With the temperature exceeding 1 500 ℃, significant amount of mullite is obtained and its amount further increases while temperature reaching up to 1 600 ℃. By changing the holding time under highest heating temperature, the degree of mullitization firstly increa- ses and then decreases. With the coal gangue dosage increasing, corundum phase peak enhances, which indicates that the increase of coal gangue dosage has negative role in synthesizing mullite. By changing the rate of silicon and aluminum from 3 ： 2 to 1 ： 1, the degree of mullitizatio ratio of silicon and aluminum is 1 ： 1, corundum phase peak disappears coal gangue with lower alumina-silica ratio is beneficial for the synthesis n gradually enhances. When the , which indicates that low-grade of mullite.
作者
杨强
宋绍雷
布乃敬
甄强
Yang Qiang Song Shaolei Bu Naijing Zhen Qiang(Pangang Group Metallurgical Materials Co. , Ltd. , Panzhihua 617000, Sichuan, China Shanghai University, Shanghai 200444, China)
出处
《钢铁钒钛》
CAS
北大核心
2017年第2期93-97,共5页
Iron Steel Vanadium Titanium
基金
国家自然科学基金(51272154)
攀枝花科知局社会发展项目(2015CY-S-1)
攀钢产学研项目(PGYCKJ006-2015)
作者简介
杨强（1969-），男，重庆合川人，硕士生，长期从事冶耐火材料、钢铁冶金辅料等无机非金属材料的生产研发。