为改善镁合金有机电泳涂层耐磨性能,通过硅烷偶联剂改性陶瓷粉体,并将陶瓷粉体充分分散于电泳漆中制得镁合金阴极电泳复合涂层,用铅笔硬度、摩擦磨损测试系统、画圈附着力方法、氯离子腐蚀试验、分别评价比较了阴极电泳涂层和加粉体后复合涂层的硬度、附着力、耐蚀性和耐磨性能。结果表明:硅烷改性Al2O3粉体的阴极电泳有机无机复合涂层厚度与不加粉体的相当,粉体的加入不会改变涂层与基体的附着力和耐蚀性,但可以增加涂层的硬度,极大地提高涂层的耐磨性。
The cathodic electrodeposition coatings（E-coatings） with silane modifying ceramics are prepared on magnesium alloy for improving the abrasion resistance of organic E-coating. corrosion resistance, circle-drawing method and abrasion resistance are evaluated by Hardness, adhesion, pencil hardness, UMT abrasion test system, and Machu test. The results show that the abrasion resistance and hardness of E-coatings are enhanced by adding Al2O3 ceramic powders. Meanwhile, corrosion resistance and adhesion of E-coatings remain unchanged.
出处
《重庆大学学报（自然科学版）》
EI
CAS
CSCD
北大核心
2014年第3期47-52,共6页
Journal of Chongqing University
基金
国家自然科学基金资助项目(50725413)
关键词
Al2O3陶瓷粉体
镁合金
阴极电泳
耐磨性
Al2O3 ceramic powders
magnesium alloy
cathode electrophoresis
abrasion resistance
作者简介
吴超云（1982-），男，博士，主要从事装备环境适应性与可靠性研究。
张津（联系人），女，北京科技大学教授，博士生导师，（E—mail）zhangjin@ustb．edu．cn。