摘要
采用室温固相复合技术制备Ag/Cu复合材料。利用拉力试验仪、扫描电镜、能谱仪等设备对Ag/Cu复合材料的剥离力、界面形貌和成分进行分析。结果表明,Ag/Cu复合材料随着轧制变形量提高,界面的剥离力逐渐增大,在轧制变形量75%时结合牢固。复合轧制结合方式符合裂纹机制。
The Ag/Cu composite was prepared by room temperature solid-phase composite technology, the stripping force and the in- terfacial morphology and component of the Ag/Cu composite were investigated with a tensile tester and the scanning electron microsco- py. The results showed that the interfacial stripping force of the Ag/Cu composite increased gradually when the deformation amount im- proved, when the deformation amount improved 75%, the Ag/Cu composite combined firmly. The composite rolling combination mode was conformed to the crack mechanism.