摘要
选取几种典型的PCD、PCBN复合片,在慢走丝电火花线切割机床上对其进行了多次加工工艺试验;运用三维表面轮廓仪、超景深三维显微镜对线切割加工后的表面粗糙度、富钴界面层加工质量、刃口加工质量等进行测量。结果表明:超硬颗粒直径大小及含量对加工质量影响较大,PCD、PCBN复合片经多次电火花线切割加工,能够得到较好的加工质量;经WEDM加工后的PCD复合片刃磨量可控制在4～15μm左右,PCBN复合片BNX20刃磨量可控制在10μm以内,而BZN6000则需较大的刃磨量。
Some typical kinds of PCD and PCBN compacts were selected to be machined by LS-WEDM, a series of processing tests were taken. After machining, the surface roughness of cutting section, the machining quality of cobalt-rich interface layer and the edge of superhard material layer were observed by 3 D optical surface profiler and optical microscope. The results showed that machining quality was affected by superhard abrasive particle size and concentration greatly, a better machining quality could be obtained after several processes of LS-WEDM; The minimum grinding allowance of PCD cutting tools can be controlled within 4 - 15 μm after LS- WEDM, and within 10 μm for PCBN BNX20, while BZN6000 needs a large follow-up workload of sharpening.
出处
《金刚石与磨料磨具工程》
CAS
2012年第3期12-17,共6页
Diamond & Abrasives Engineering
基金
国家自然科学基金重大项目(20890024)
国家重点基础研究发展计划(2007CB714502)
关键词
聚晶金刚石
聚晶立方氮化硼
金刚石复合片
电火花线切割
polycrystalline diamond （ PCD ）
polyerystalline cubic boron nitride （ PCBN ）
polycrystalline diamond compact（PDC）
wire electric discharge machining（WEDM）
作者简介
宋满仓，男，1964年生，博士，副教授，主要从事模具设计与制造技术及放电加工工艺的研究。E-mail：mcsong@dlut．edu．cn
张建磊，男，1986年生，硕士研究生，主要从事电加工技术的研究。E-mail：skdzjl_001@126．com
王华，男，1973年生，硕士，高级工程师，主要从事放电加工技术的研究。E-mail：h．wang@meach．cn
于超，男，1985年生，硕士研究生，主要从事电加工技术的研究。E-mail：smiletofacelife@163．com
王敏杰，男，1958年生，工学博士，教授，博士生导师，主要从事模具技术、高速切削与先进制造技术、高分子材料成型技术和水中航行体流体动力学的研究。E-mail：mjwang@dlut．edu．cn
刘冲，男，1963年生，工学博士，教授，博士生导师，主要从事微机电系统（MEMS）、生化微传感器、物联网技术和精密仪器与测试技术的研究。E-mail：chongl@dlut．edu．cn