研制的603耐高温环氧树脂体系的Tg约为225℃,热分解温度约为387℃;采用凝胶时间、DSC和流变特性表征了其固化反应特性,确定了固化工艺;603树脂体系可以湿法和热熔法制备预浸料,预浸料铺覆工艺性优异,T700/603和T800/603复合材料可作为高性能复合材料结构件使用。
The 603 is a heat-resistant epoxy resin.Its glass transition temperature and heat decomposition temperature are 225℃ and 387℃ respectively.The solidifying characteristics are studied by gel-time,DSC and rheology,and then its curing technique is confirmed.Draping prepregs can be made through solvent and melting.The composites of T700/603 and T800/603 can be used as structural components with high performance.