为了研究制备复合隐身粒子的方法,采用溶胶-凝胶法制备了核-壳结构SiO2@Bi2O3粒子.通过XRD、TEM及发射率测试仪对制备的材料的结构、形貌和性能进行了表征.XRD表明在700℃可以得到Bi2O3纯相;红外发射率测试表明,Bi2O3具有较低的红外发射率,在SiO2表面包覆Bi2O3后,在3～5μm和8～14μm两个测试波段都能降低SiO2的红外发射率.通过核-壳结构的形式,在较高发射率的样品表面涂覆红外发射率较低的样品,可以提高红外隐身效果.
In order to provide a method for developing composite stealth particles,SiO2@ Bi2O3 particles with spherical core-shell structure were prepared by sol-gel method. The structure,morphology and emissivity of the particles were characterized by XRD,TEM and infrared emissometer. XRD measurement indicates that the pure phase of Bi2O3can be obtained at 700 ℃. TEM validates the formation of core-shell structure of SiO2@ Bi2O3 spheres. The IR emissivity measurements indicate that the high emissivity of SiO2 in the ranges of 3 ～ 5 μm and 8 ～ 14 μm can be lowered by coating a thin layer of Bi2O3 on the surface of SiO2 spheres. Therefore,the as-synthesized core-shell structured SiO2@ Bi2O3 spheres can improve the IR shielding property.
出处
《材料科学与工艺》
EI
CAS
CSCD
北大核心
2010年第1期43-45,共3页
Materials Science and Technology
基金
国家自然科学基金重大研究计划资助项目(90505008)
国家自然科学基金资助项目(60471005)
中国博士后科学基金资助项目(第39批)
江苏省博士后科研资助计划(2006年度第一批)
关键词
核-壳结构
红外发射率
氧化铋
core-shell structure
infrared emissivity
bismuth oxide
作者简介
E-mail：shaocm2008@yahoo．com．cn.作者简介：邵春明（1982-），男，博士；
徐国跃（1958-），男，教授，博士生导师．