在过氧化苯甲酰(BPO)引发下,以丁酮为溶剂,采用溶液聚合法合成了苯乙烯-马来酸酐共聚物,并详细研究了温度、引发剂用量、苯乙烯与马来酸酐配比、单体(苯乙烯与马来酸酐)质量分数及聚合时间对聚合反应的影响。研究表明,在温度80℃,x(BPO)=0.6%(相对于苯乙烯与马来酸酐),n(苯乙烯)∶n(马来酸酐)=1∶1,w(单体)=15%(相对于混合溶液),反应时间4 h的条件下,聚合物收率可达99%。采用13CNMR、IR、GPC、元素分析对共聚物结构进行了表征。利用TG测定了其热稳定性。结合共聚物的元素分析与13CNMR的分析结果,表明合成的苯乙烯-马来酸酐共聚物是一种交替共聚物。
Styrene-maleic anhydride copolymer was synthesized by the solution polymerization method,with benzoyl peroxide（BPO） as initiator and butanone as solvent.The influence of polymerization temperature,initiator dosage,ratio of styrene to maleic anhydride,monomer（styrene and maleic anhydride） mass fraction and reaction time on polymerization was discussed in detail.The research showed that the yield of the copolymer reached 99% under the conditions of 80 ℃ of the polymerization temperature,0.6% of initiator dosage,1∶1 of molar ratio of styrene to maleic anhydride,15% of monomer mass fraction and 4 h of reaction time.The structure of the copolymer was confirmed by 13CNMR、IR、GPC and elementary analysis.The thermal stability of the copolymer was tested by TG.Based on the analysis results of elementary analysis and ^13CNMR of the product,the structure of styrene-maleic anhydride copolymer was confirmed to be the alternating copolymer.
出处
《精细化工》
EI
CAS
CSCD
北大核心
2010年第3期217-221,共5页
Fine Chemicals
基金
国家自然科学基金青年基金(20804007)
教育部高等学校博士学科点专项科研基金(200801411032)
教育部长江学者和创新团队发展计划(IRT0711)~~
关键词
苯乙烯
马来酸酐
交替共聚物
溶液聚合
功能材料
styrene
maleic anhydride
alternating copolymer
solution polymerization
functional materials
作者简介
唐炳涛（1976-），男，博士，研究方向为光转换功能分子的设计合成与精细化工清洁合成新技术，E—mail：tangbt@dlut．edu．cn。