模具表面球冠状微凸体形貌的激光加工 被引量:3

Laser texturing of spherical cap slight protuberance profile on mould & die surface
在线阅读 下载PDF
导出
摘要 为了减少磨损,延长模具的使用寿命,在模具表面应用激光毛化处理。采用200W灯抽运Nd:YAG激光器,进行系统的激光毛化工艺试验,得出脉冲激光参量对模具表面微观形貌主要几何参量的影响规律,最终获得了预期的几何形貌。并分别测量和分析了毛化模具表面硬度和金相组织状况。结果表明,微凸体表面硬度比基体材料的表面硬度提高了30%~40%,提高了模具表面的耐磨性。 With the aim of reducing wear and prolonging working life of a mould & die, laser texturing technology was applied to the surface of the mould & die. In the experiment,a 200W lamp pumped Nd:YAG laser was adopted to process the mould & die surface. Then the rule of the effect of laser parameters on the micro profile of the mould & die was obtained after experiments. Finally, the expected profile was obtained. The surface hardness and metallographic structure were measured and analyzed. The results showed that the surface hardness of slight protuberance was improved 30% - 40% compared with that of the substrate and the wear resistance of mould & die was improved too.
出处 《激光技术》 CAS CSCD 北大核心 2009年第5期500-502,共3页 Laser Technology
基金 国家自然科学基金资助项目(50475122)
关键词 激光技术 激光毛化 表面形貌 工艺试验 模具 laser technique laser texturing surface roughness profile process experiment mould & die
作者简介 米涛(1982-),男,硕士研究生,主要从事特种模具的研究。 通讯联系人。E-mail:fyh@ujs.edu.cn
  • 相关文献

参考文献8

二级参考文献12

  • 1陈光南.毛化轧辊的新方法及其应用[J].应用激光,1996,16(4):155-158. 被引量:26
  • 2刘莹.[D].北京:清华大学,2003.
  • 3[3]Pfestorf M,Engel U,Geiger M. J Mach Tools Manufact,1998,38(5-6): 607~614.
  • 4[4]Tzeng Y F. J Mater Proc Technol,2000,102: 40~47.
  • 5[2]C L Chan,J Mazumder,The effect of radiative heat lost on laser material damage[J].J.Appl.Phys.,1988,63(12):5890.
  • 6[3]M Ii,T P Duffey,J Mazumder.Spatially and temporally resolved temperature measurements of plasma generated in percussion drilling with a diode-pumped Nd:YAG laser[J].J.Appl.Phys.,1998,84(8):4122.
  • 7Geiger M, Roth S , Becker. Influence of laser-produced microstructure on the tribology behaviorof ceramics. Surface & Coating Technology, 1998, (100-101): 17-22.
  • 8Minamida, Katsuhiro. Laser system for dulling work roll by Q-switehed Nd: YAG laser. Nippon Steel Technical Report. 1990,4:30-34.
  • 9Yamada Y, Saisu M. Development of image clarity steel sheet laser mirror. In: Mechanical Working and Steel Processing Conference Proceedings V, 1990:21-24.
  • 10朱大庆,左都罗,李适民,刘建功.激光刻花表面形貌的数值模拟及实验比较[J].华中理工大学学报,2000,28(1):68-70. 被引量:3

共引文献36

同被引文献17

  • 1田丽梅,任露泉,韩志武,施卫平,丛茜.仿生非光滑表面脱附与减阻技术在工程上的应用[J].农业机械学报,2005,36(3):138-142. 被引量:45
  • 2陈光南.毛化轧辊的新方法及其应用[J].应用激光,1996,16(4):155-158. 被引量:26
  • 3段军.激光微加工磁盘——激光毛化技术现状与发展[J].激光技术,2006,30(5):490-493. 被引量:5
  • 4万轶,熊党生.激光表面织构化改善摩擦学性能的研究进展[J].摩擦学学报,2006,26(6):603-607. 被引量:77
  • 5Andersson P. Microlubrication Effect by Laser--tex- tured Steel[J]. Wear,2007,262(3/4) :369-279.
  • 6Barber G C, Gao H. Experimental Study on the Fric- tion Characteristics of Laser- textured Steel Sheets during Metal Forming Process [C]//Proeeedings of 2004 ASME/STLE International Joint Tribology Con- ference. Long Beach, 2004: 1567-1576.
  • 7Vilhena L M, Sedlacek M, Podgornik B,et al. Sur- face Texturing by Pulsed Nd: YAG Laser[J]. Tri- bology International, 2009 , 42 : 1496-1504.
  • 8Kovalchenko A, Ajayi O, Erdemir A. The Effect of Laser Surface Texturing on Transitions in Lu- brication Regimes during Unidi Rectional Sliding Contact[J]. Tribology International, 2005,38 : 219 -225.
  • 9Borghi A, Gualtieri E, Marchetto D,et al. Tribo- logical Effects of Surface Texturing on Nitriding Steel for High--performance Engine Applicationst[J]. Wear, 2008, 265:1046-1051.
  • 10Skopp A, Woydt M, Habig K H. Unlubricated Sliding Frictionand Wear of Various Si3N4 Pairs between 22- 1000 ℃[J]. Tribology International, 1980, 12(3): 153-158.

引证文献3

二级引证文献18

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部