摘要
采用化学共沉淀法与溶胶-凝胶法相结合,在制备过程中改变磁性纳米粒子和TEOS的引入方式,成功地制备了多核超顺磁性Ni0.5Zn0.5Fe2O4/SiO2催化剂载体.采用透射电子显微镜(TEM)、氮气吸附、X射线衍射(XRD)及物理性质综合测试系统(PPMS)对样品进行了表征,利用永磁铁对载体的分离效果进行了验证.研究结果表明,改进制备方法后,制备的载体比表面积明显增大,这有利于催化剂在载体上的分散与固载;样品的饱和磁化强度明显增加,表明样品具有很好的磁响应能力,有利于催化剂的分离,同时,载体的超顺磁特性也有利于液相催化体系中催化剂的分散.
A muhicore superparamagnetic Ni0.5 Zn0.5 Fe2O4/SiO2 catalyst support was synthesized by slightly modifying the conventional preparation method, namely, altering the manner of introducing Ni0.5 Zn0.5 Fe2O4 nanoparticles into TEOS. The modified method resulted in a great increase in specific surface area, saturation magnetization of Ni0.5 Zn0.5 Fe2O4/SiO2 and better separation in liquid system. The synthesized catalyst supports were characterized by means of X-ray diffraction, N2 gas adsorption-desorption experiments, transmission electron microscopy and a physical properties measurement system（PPMS）.
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2008年第7期1428-1431,共4页
Chemical Journal of Chinese Universities
基金
黑龙江省青年基金(批准号:QC07C20)
黑龙江省教育厅科研项目基金(批准号:11511129
1152G018
YJSCX2007-0318HLJ)
哈尔滨师范大学骨干教师科研项目基金(批准号:KG2005-01)
哈尔滨市青年基金(批准号:2007RFQXG060)资助
关键词
超顺磁性
多核
催化剂分离
饱和磁化强度
比表面积
Superparamagneticity
Multicore
Catalyst surport separation
Saturation magnetization
Specific surface area
作者简介
联系人简介：苏文辉，男，教授，博士生导师，主要从事高压下复合氧化物纳米固体材料的制备、表征及高压对于其内部微结构和界面微观状态的影响方面的研究。E-mail：hsdzkx@163.com