Nano-SiO2 was modified using silane coupling agent （KH-550） and hyperbranched poly（amine-ester） respectively, and Poly（vinyl chloride） （PVC）/modified nano-SiO2 composites were made by melt-blending. The composites＇ structures andmechanical properties were characterized by transmission electron microscopy（TEM）, sanning electronic microscopy（SEM） and electronic universal testing machine. The results. show that nano-SiO2 grafted by hyperbranched poly （amine-ester） increases obviously in dispersion in PVC matrix, and mechanical properties of PVC are effectively improved. Moreover, it was found that mechanical properties of PVC/nano-SiO2 composites reach the best when weight percent of nano-SiO2 in PVC matrix is 1%. Compared with crude PVC, the tensile strength of hyperbranched poly （amine-ester） grafted nano-SiO2/ PVC composite increases by 24.68 % and its break elongation, flexural strength and impact strength increase by 15.73%, 4.07% and 1 841.84%, respectively. Moreover, the processing of the composites is improved.
Nano-SiO2 was modified using silane coupling agent （KH-550） and hyperbranched poly（amine-ester） respectively, and Poly（vinyl chloride） （PVC）/modified nano-SiO2 composites were made by melt-blending. The composites＇ structures andmechanical properties were characterized by transmission electron microscopy（TEM）, sanning electronic microscopy（SEM） and electronic universal testing machine. The results. show that nano-SiO2 grafted by hyperbranched poly （amine-ester） increases obviously in dispersion in PVC matrix, and mechanical properties of PVC are effectively improved. Moreover, it was found that mechanical properties of PVC/nano-SiO2 composites reach the best when weight percent of nano-SiO2 in PVC matrix is 1%. Compared with crude PVC, the tensile strength of hyperbranched poly （amine-ester） grafted nano-SiO2/ PVC composite increases by 24.68 % and its break elongation, flexural strength and impact strength increase by 15.73%, 4.07% and 1 841.84%, respectively. Moreover, the processing of the composites is improved.
基金
Sponsored by the Ministerial Level Advanced Research Foundation (120701BQ0126)
作者简介
LI Jie （1967 - ）, associate professor, Ph. D., leejie@bit.edu.cn.