摘要
采用机械合金化的方法制备出Ｍｎ７０Ｂｉ３０纳米晶粉末。通过Ｘ射线衍射和饱和磁化强度的测量，研究了球磨过程中样品的结构和磁性的变化。Ｘ射线衍射的测量结果表明，Ｂｉ在Ｍｎ中的固溶度随球磨时间的增加而增加。球磨８０ｈ后，Ｂｉ的固溶度趋于稳定，此时粉末的晶粒尺寸达到１４ｎｍ。球磨初期，样品的饱和磁化强度（σｓ）随球磨时间的增加而增加。球磨１５ｈ，σｓ从零增加到最大值。之后，σｓ随球磨时间的增加而减小。饱和磁化强度的测量结果表明，反铁磁性的Ｍｎ元素和抗磁性的Ｂｉ元素通过机械合金化产生了铁磁性。
Nanocrystalline Mn 70 Bi 30 powders have been synthesized by mechanical alloying process. X ray diffraction and saturation magnetization(σ s) measurements were used to analyze the changes of structure and magnetic properties of the powders during different milling times. The results show that under the condition of high energy milling, the Mn 70 Bi 30 powders may reach a nanometer scale and the antiferromagnetic Mn and the diamagnetic Bi may produce ferromagnetic Mn 70 Bi 30 powders in process of mechanical alloying.