The conjugation of semi-solid process technique and casting-rolling technique applied to produce the magnesium strips was studied. The semi-solid slurry has been prepared continuously by the mechanical method and its temperature was controlled strictly at the same time. AZ91D and AZ31 casting magnesium alloys were applied to the experiment. The casting-rolling strips with non-dendritic structure were obtained and its main mechanical property is better. The process ability of the casting-rolling strips was studied. It is significative to link the semi-solid process techniques and casting-rolling techniques, through which we can get high quality magnesium alloy strips with non-dendritic structure and improve the overall properties of the products.
The conjugation of semi-solid process technique and casting-rolling technique applied to produce the magnesium strips was studied. The semi-solid slurry has been prepared continuously by the mechanical method and its temperature was controlled strictly at the same time. AZ91D and AZ31 casting magnesium alloys were applied to the experiment. The casting-rolling strips with non-dendritic structure were obtained and its main mechanical property is better. The process ability of the casting-rolling strips was studied. It is significative to link the semi-solid process techniques and casting-rolling techniques, through which we can get high quality magnesium alloy strips with non-dendritic structure and improve the overall properties of the products.
基金
National Natural Science Foundation of China(Grant Nos.50175006,50374014).
作者简介
Prof., Ph.D., to whom correspondence should be addressed, E-mail： xiess@grinm.com.