以钼矿尾矿为主要原料(55%),结合高岭土、红泥、长石、玻璃粉及发泡剂,烧结制备了保温陶瓷板,并对其进行了表面装饰。测定了保温陶瓷板的吸水率、体积密度、抗压强度、导热系数,观测了其显微结构并对气孔孔径进行了统计。研究了烧成温度、泥浆细度以及发泡剂添加量对保温陶瓷板的孔径影响规律。结果表明:发泡剂添加量对保温陶瓷板的孔结构、孔径大小及分布影响最为显著,是获得低导热系数保温陶瓷板的关键。钼矿尾矿基隔热保温板固废含量高、隔热保温性能优异且质轻,是一种具有广阔市场前景的新型建筑保温材料。
The insulating ceramic plate was sintered and surface-decorated using molybdenum tailings as the main raw material(55%)with kaolin,red sludge,feldspar,glass powder and blowing agent incorporated.The water absorption,bulk density,compressive strength and thermal conductivity of the insulating ceramic plate were measured,and the microstructure was observed and the pore diameter was counted.The effects of firing temperature,slurry fineness and addition of blowing agent on the pore size of insulating ceramic plates were studied.The results show that the addition of blowing agent has the most significant influence on the pore structure,pore size and distribution of the insulating ceramic plate,and is the key to obtain low thermal conductivity.In this study,the prepared molybdenum mine tailings-based insulating ceramic plate has high solid content,excellent thermal insulation performance and light weight,and is surely a new building insulation material with broad market prospects.
作者
李坤
刘娥
卢庆阳
LI Kun;LIU E;LU Qingyang(Xianyang Research&Design Institute of Ceramics Co.,Ltd.,Xianyang 712000,Shaanxi,China)
出处
《硅酸盐学报》
EI
CAS
CSCD
北大核心
2020年第3期416-422,共7页
Journal of The Chinese Ceramic Society
基金
陕西省“13115”科技创新工程计划(2017ZDXM-SF-106)资助.
关键词
钼矿尾矿
导热系数
保温陶瓷板
发泡剂
molybdenum mine tailings
thermal conductivity
insulating ceramic plate
blowing agent
作者简介
第一作者:李坤(1987—),男,博士,工程师,E-mai:blueonblue@whut.edu.cn,武汉理工大学材料科学与工程专业博士,咸阳陶瓷研究设计院有限公司工程师,主要从事工业及建筑陶瓷材料的研究及应用。发表SCI论文四篇;参与“十三五”国家重点研发计划项目“工业及城市大宗固废制备绿色建材关键技术研究与应用”,西藏自治区合作项目“西藏文化元素抽取与陶瓷工艺品制造关键技术及应用示范”,企业合作项目“透辉石陶瓷仿古砖及其坯体增白技术的研究”等,通信作者:刘娥(1965—),女,学士,教授级高级工程师,E-mai:Liu-e-2007@163.com,咸阳陶瓷研究设计院有限公司教授级高级工程师,主要从事工业及建筑陶瓷的研究开发及产业化应用。以第一作者发表论文10篇,申请发明专利5项。主持及参与国家重点研发计划项目“利用风积沙制备烧结透水材料的研究与应用”,科技部科研院所基金项目“利用陶瓷废料生产干挂陶瓷板的研究开发”,陕西省“13115”科技产业化项目“利用建筑垃圾和煤矸石制作保温陶瓷砖的研究与开发”,陕西省重点研发计划项目“利用钼矿尾矿生产低导热系数墙体材料的研究开发”等。