通过旋蒸法制备了Cu/ZSM-5、Fe/ZSM-5和Fe-Cu/ZSM-53种样品,使用X射线粉末衍射(XRD)、N2-吸附/脱附、氢气程序升温还原(H2-TPR)、氨气程序升温脱附(NH3-TPD)技术对其进行了表征,并研究了其NH3-SCR催化还原NO性能。实验结果表明,Fe和Cu双金属改性Fe-Cu/ZSM-5样品催化性能优异,具有较宽的反应活性温度窗口,在200~560℃范围内的转化率均超过90%,在290~400℃下转化率可达到98%以上。Fe-Cu/ZSM-5样品优异的催化性能与其具有丰富的中酸性位和良好的氧化还原性能密切相关。
Cu/ZSM-5,Fe/ZSM-5and Fe-Cu/ZSM-5catalysts were prepared by the method of spin evaporation for the selective catalytic reduction of NOx with NH3.The properties of the prepared catalysts were characterized by XRD,BET,H2-TPR and NH3-TPD technologies.The results shown that Fe and Cu bimetal modification of Fe-Cu/ZSM-5catalyst had excellent catalytic activity,and shown a wide activity temperature window.The catalytic efficiency of Fe-Cu/ZSM-5was more than 90%within the scope of 200~560℃,and reached above 98%within the scope 290~400℃.This catalytic activity related with its abundant acid sites and great redox properties.
作者
其其格吉日嘎拉
李晨曦
叶青
程锦
程水源
康天放
Munkhjargal;Tsetsegjargal;Li Chenxi;Ye Qing;Cheng Jin Cheng;Shuiyuan;Kang Tianfang(Key Laboratory of Beijing on Regional Air Pollution Control,Beijing University of Technology,Beijing 100124)
出处
《化工新型材料》
CAS
CSCD
北大核心
2020年第2期179-184,190,共7页
New Chemical Materials
基金
国家自然科学基金项目(21277008、20777005)
国家重点研发计划项目(2017YFC0209905).
作者简介
其其格吉日嘎拉(1984-),女,博士研究生,主要研究方向为大气污染控制化学;联系人:叶青,教授,博士生导师,主要研究方向为环境催化和大气污染控制。