Laser Induced Breakdown Spectroscopic(LIBS)technique was used to detect calcium and silicon in an unknown sample.In this method plasma was generated by Nd∶YAG laser of wavelength 1 064 nm with energy 400 mJ and pulse...Laser Induced Breakdown Spectroscopic(LIBS)technique was used to detect calcium and silicon in an unknown sample.In this method plasma was generated by Nd∶YAG laser of wavelength 1 064 nm with energy 400 mJ and pulse duration between 5~10ns.The method was applied for the qualitative as well as quantitative analysis.In the qualitative analysis,the electron number density(Ne)of plasma containing calcium and silicon is determined showing that Neof neutral particles is equivalent to 1016(cm-3)whereas for ionized particles it is 1017(cm-3).Plasma temperature is measured using Boltzmann plot method which must be greater than 10 000 k.Intensity ratio method is used for the quantitative analysis shows various elements in abundance with calcium and silicon in majority.展开更多
Surface Preparation is very important in adhesive b on ding of spray coatings to the surface of a work piece. The common practice is gr it-blasting of the surface before subjecting it to the spray coating process. In ...Surface Preparation is very important in adhesive b on ding of spray coatings to the surface of a work piece. The common practice is gr it-blasting of the surface before subjecting it to the spray coating process. In this study, grit-blasting of an AISI 4130 steel (of different heat treatmen ts) with Al 2O 3 particles was studied. Various grit-blasting parameters such as blasting particle size, the distance between blasting nozzle and the work pi ece (25, 30 and 40 cm.), blasting pressure (3,4,5,6 and 7 bars), blasting time ( 3, 6 and 10 seconds), and the blasting angle (45° and 90°) were examined in or der to find the optimum roughness. The mean roughness (Ra) of the grit-blasted surfaces were measured and the vari ations of the roughness with respect to the above mentioned variables were studi ed. The results show that by increasing blasting time, surface roughness increas es up to a maximum and then slightly decreases it with further duration of t he process. On the other hand a lengthy blasting causes some undesirable results such as an increase in residual particles between surface irregularities. There fore an optimum blasting time is of great importance. Increasing the blasting pr essure also provides a rougher surface, but in grit blasting of harder specimens the surface roughness decreases when the pressure reaches a certain limit. About the blasting angle, it was noticed that an angle of 45° results in less r esidual particles between the surface irregularities, in comparison to the angle of 90°. After grit-blasting, the specimens were plasma spray coated with 80% ZrO 2-20 % Y 2O 3 powder. The adhesive strength of the coating to the substrate was the n measured according to the DIN 50160 standard. The results show that for a certain base metal, the adhesive strength is directl y related to the surface roughness of the base material. Residual particles afte r grit-blasting the surface of the specimens can also have a strong deteriorati ng effect on adhesive strength. Finally, it was shown that the hardness of the b ase material had a direct effect on the adhesive strength of the sprayed coating s.展开更多
A sputtering-type microwave multipolar ECR plasma processing for preparing thin films, is built with Nd-Fe-B magnets and 2.45 GHz, TE<sub>10</sub> mode microwave. The plasma distributions in the axial dire...A sputtering-type microwave multipolar ECR plasma processing for preparing thin films, is built with Nd-Fe-B magnets and 2.45 GHz, TE<sub>10</sub> mode microwave. The plasma distributions in the axial direction, which is important for preparing thin films, are found to be very sensitive to the magnetic potential fields in plasma chamber. The plasma parameters are also influenced by the background gas pressure.展开更多
文摘Laser Induced Breakdown Spectroscopic(LIBS)technique was used to detect calcium and silicon in an unknown sample.In this method plasma was generated by Nd∶YAG laser of wavelength 1 064 nm with energy 400 mJ and pulse duration between 5~10ns.The method was applied for the qualitative as well as quantitative analysis.In the qualitative analysis,the electron number density(Ne)of plasma containing calcium and silicon is determined showing that Neof neutral particles is equivalent to 1016(cm-3)whereas for ionized particles it is 1017(cm-3).Plasma temperature is measured using Boltzmann plot method which must be greater than 10 000 k.Intensity ratio method is used for the quantitative analysis shows various elements in abundance with calcium and silicon in majority.
文摘Surface Preparation is very important in adhesive b on ding of spray coatings to the surface of a work piece. The common practice is gr it-blasting of the surface before subjecting it to the spray coating process. In this study, grit-blasting of an AISI 4130 steel (of different heat treatmen ts) with Al 2O 3 particles was studied. Various grit-blasting parameters such as blasting particle size, the distance between blasting nozzle and the work pi ece (25, 30 and 40 cm.), blasting pressure (3,4,5,6 and 7 bars), blasting time ( 3, 6 and 10 seconds), and the blasting angle (45° and 90°) were examined in or der to find the optimum roughness. The mean roughness (Ra) of the grit-blasted surfaces were measured and the vari ations of the roughness with respect to the above mentioned variables were studi ed. The results show that by increasing blasting time, surface roughness increas es up to a maximum and then slightly decreases it with further duration of t he process. On the other hand a lengthy blasting causes some undesirable results such as an increase in residual particles between surface irregularities. There fore an optimum blasting time is of great importance. Increasing the blasting pr essure also provides a rougher surface, but in grit blasting of harder specimens the surface roughness decreases when the pressure reaches a certain limit. About the blasting angle, it was noticed that an angle of 45° results in less r esidual particles between the surface irregularities, in comparison to the angle of 90°. After grit-blasting, the specimens were plasma spray coated with 80% ZrO 2-20 % Y 2O 3 powder. The adhesive strength of the coating to the substrate was the n measured according to the DIN 50160 standard. The results show that for a certain base metal, the adhesive strength is directl y related to the surface roughness of the base material. Residual particles afte r grit-blasting the surface of the specimens can also have a strong deteriorati ng effect on adhesive strength. Finally, it was shown that the hardness of the b ase material had a direct effect on the adhesive strength of the sprayed coating s.
文摘A sputtering-type microwave multipolar ECR plasma processing for preparing thin films, is built with Nd-Fe-B magnets and 2.45 GHz, TE<sub>10</sub> mode microwave. The plasma distributions in the axial direction, which is important for preparing thin films, are found to be very sensitive to the magnetic potential fields in plasma chamber. The plasma parameters are also influenced by the background gas pressure.
文摘流程工业颗粒物成分的在线检测具有低延时、安全可靠及低成本等要求,目前没有适合的技术手段.微波等离子炬(Microwave plasma torch,MPT)原子发射光谱法具有直接进样、成本低及装置安全可靠等优点,有潜力成为工业在线检测的重要手段.本文基于MPT装置对水泥样品进行直接进样分析,并针对工业应用场景中标准样品受限的问题,采用单样本定标技术(Single sample calibration,SSC)进行定量分析.SSC法中的线性假设容易受到等离子体参数波动的影响,导致精度下降.为此,提出了一种基于参数标准化的SSC算法PS-SSC(SSC based on parameter standardization),通过激发温度和电子数密度对谱线强度进行修正以提高SSC的定量精度.为了评估MPT和PS-SSC方法联用在水泥成分快速分析中的有效性,将GSB 08-2985-2013标准水泥粉末气溶胶直接引入MPT中进行定量分析,并将PS-SSC与现有定量方法进行比较.与传统SSC方法相比,PS-SSC方法的决定系数R2由‒0.81~0.81提高到0.39~0.88,平均相对误差由4.39%~10.33%提高到1.55%~5.83%,平均相对标准偏差由2.89%~9.40%提高到2.28%~6.50%,展现了该方法在工业在线成分检测中的应用潜力.