In this paper, a high calcium high sulfate ash as the main material, adding fly ash, lime, cement, gypsum and some modifiers to prepare autoclaved aerated concrete. The products complies with the technical requirement...In this paper, a high calcium high sulfate ash as the main material, adding fly ash, lime, cement, gypsum and some modifiers to prepare autoclaved aerated concrete. The products complies with the technical requirements of GB/T11968-2006. This paper also studies the influence of the physical methods and water ratio on autoclaved aerated concrete by high calcium high sulfate ash aerated concrete. The best ratio of water and Grinding time were found in practice study.展开更多
为改善高钙粉煤灰在混凝土中的体积安定性和水化活性,本文对高钙粉煤灰进行了CO_(2)矿化改性,研究了不同CO_(2)矿化反应时长下高钙粉煤灰的固碳量和游离氧化钙含量,及CO_(2)矿化改性高钙粉煤灰对水泥砂浆水化热、力学性能和孔隙结构的...为改善高钙粉煤灰在混凝土中的体积安定性和水化活性,本文对高钙粉煤灰进行了CO_(2)矿化改性,研究了不同CO_(2)矿化反应时长下高钙粉煤灰的固碳量和游离氧化钙含量,及CO_(2)矿化改性高钙粉煤灰对水泥砂浆水化热、力学性能和孔隙结构的影响。结果表明,经12 h CO_(2)矿化改性处理,高钙粉煤灰固碳量可超过10%(质量分数),高钙粉煤灰中的游离氧化钙含量明显降低。随着矿化反应时间的延长,掺高钙粉煤灰的水泥浆体水化诱导期缩短,早期水化放热量明显降低。CO_(2)矿化改性处理还能减轻高钙粉煤灰对水泥砂浆强度的负面影响,改善水泥砂浆孔隙结构,降低孔隙率和大孔含量,促进水泥的早期水化和水化硅酸钙的成核结晶。展开更多
文摘In this paper, a high calcium high sulfate ash as the main material, adding fly ash, lime, cement, gypsum and some modifiers to prepare autoclaved aerated concrete. The products complies with the technical requirements of GB/T11968-2006. This paper also studies the influence of the physical methods and water ratio on autoclaved aerated concrete by high calcium high sulfate ash aerated concrete. The best ratio of water and Grinding time were found in practice study.
文摘为改善高钙粉煤灰在混凝土中的体积安定性和水化活性,本文对高钙粉煤灰进行了CO_(2)矿化改性,研究了不同CO_(2)矿化反应时长下高钙粉煤灰的固碳量和游离氧化钙含量,及CO_(2)矿化改性高钙粉煤灰对水泥砂浆水化热、力学性能和孔隙结构的影响。结果表明,经12 h CO_(2)矿化改性处理,高钙粉煤灰固碳量可超过10%(质量分数),高钙粉煤灰中的游离氧化钙含量明显降低。随着矿化反应时间的延长,掺高钙粉煤灰的水泥浆体水化诱导期缩短,早期水化放热量明显降低。CO_(2)矿化改性处理还能减轻高钙粉煤灰对水泥砂浆强度的负面影响,改善水泥砂浆孔隙结构,降低孔隙率和大孔含量,促进水泥的早期水化和水化硅酸钙的成核结晶。