The hot compressive deformation behaviors of ZHMn34-2-2-1 manganese brass are investigated on Thermecmastor-Z thermal simulator over wide processing domain of temperatures （923–1073 K） and strain rates （0.01–10 s...The hot compressive deformation behaviors of ZHMn34-2-2-1 manganese brass are investigated on Thermecmastor-Z thermal simulator over wide processing domain of temperatures （923–1073 K） and strain rates （0.01–10 s^–1）. The true stress–strain curves exhibit a single peak stress, after which the stress monotonously decreases until a steady state stress occurs, indicating a typical dynamic recrystallization. The analysis of deviation between strain-dependent Arrhenius type constitutive and experimental data revealed that the material parameters （n, A, and Q） for the ZHMn34-2-2-1 manganese brass are not constants but varies as functions of the deformation conditions. A revised strain-independent sine hyperbolic constitutive was proposed, which considered the coupled effects of strain rate temperature and strain on material parameters. The correlation coefficient and the average absolute relative error are used to evaluate the accuracy of the established constitutive model. The quantitative results indicate that the proposed constitutive model can precisely characterize the hot deformation behavior of ZHMn34-2-2-1 manganese brass.展开更多
This study was done to evaluate the nugget zone(NZ)corrosion behavior of dissimilar copper/brass joints welded by friction stir lap welding(FSLW)in a solution of 0.015 mol/L borax(pH 9.3).To this end,dissimilar copper...This study was done to evaluate the nugget zone(NZ)corrosion behavior of dissimilar copper/brass joints welded by friction stir lap welding(FSLW)in a solution of 0.015 mol/L borax(pH 9.3).To this end,dissimilar copper/brass plates were welded with two dissimilar heat inputs(low and high)during the welding procedure.The high and low heat inputs were conducted with 710 r/min,16 mm/min and 450 r/min,25 mm/min,respectively.Using open circuit potential(OCP)measurements,electrochemical impedance spectroscopy(EIS)and Tafel polarization tests,the electrochemical behavior of the specimens in borate buffer solution was assessed.With the help of scanning electron microscope(SEM),the morphology of welded specimen surfaces was examined after immersion in the test solution.According to the results,the NZ grain size and resistance improvement reduced due to the nugget zone corrosion with a decreased heat input.The results obtained from Tafel polarization and EIS indicated the improved corrosion behavior of the welded specimen NZ with a decrease in the heat input during the welding process unlike the copper and brass metals.Furthermore,an increased heat input during the welding process shows a reduction in the conditions for forming the passive films with higher protection behavior.展开更多
The processing of sintered brass products is described. The effect of processing parameters on the mechanical properties of the products is discussed. The relationship between the main mechanical properties and the f...The processing of sintered brass products is described. The effect of processing parameters on the mechanical properties of the products is discussed. The relationship between the main mechanical properties and the friction and wear characteristics is analyzed. The tribological behaviour of the material is determined under different conditions (speed, load, time, environment etc). Comparison is made with that of dense products. The friction and wearmechanisms are investigated. Results are instructive to the application of the material.展开更多
基金Project(2012ZX04010-081) supported by the National Science and Technology Major Project of the Ministry of Science and Technology of China
文摘The hot compressive deformation behaviors of ZHMn34-2-2-1 manganese brass are investigated on Thermecmastor-Z thermal simulator over wide processing domain of temperatures （923–1073 K） and strain rates （0.01–10 s^–1）. The true stress–strain curves exhibit a single peak stress, after which the stress monotonously decreases until a steady state stress occurs, indicating a typical dynamic recrystallization. The analysis of deviation between strain-dependent Arrhenius type constitutive and experimental data revealed that the material parameters （n, A, and Q） for the ZHMn34-2-2-1 manganese brass are not constants but varies as functions of the deformation conditions. A revised strain-independent sine hyperbolic constitutive was proposed, which considered the coupled effects of strain rate temperature and strain on material parameters. The correlation coefficient and the average absolute relative error are used to evaluate the accuracy of the established constitutive model. The quantitative results indicate that the proposed constitutive model can precisely characterize the hot deformation behavior of ZHMn34-2-2-1 manganese brass.
文摘This study was done to evaluate the nugget zone(NZ)corrosion behavior of dissimilar copper/brass joints welded by friction stir lap welding(FSLW)in a solution of 0.015 mol/L borax(pH 9.3).To this end,dissimilar copper/brass plates were welded with two dissimilar heat inputs(low and high)during the welding procedure.The high and low heat inputs were conducted with 710 r/min,16 mm/min and 450 r/min,25 mm/min,respectively.Using open circuit potential(OCP)measurements,electrochemical impedance spectroscopy(EIS)and Tafel polarization tests,the electrochemical behavior of the specimens in borate buffer solution was assessed.With the help of scanning electron microscope(SEM),the morphology of welded specimen surfaces was examined after immersion in the test solution.According to the results,the NZ grain size and resistance improvement reduced due to the nugget zone corrosion with a decreased heat input.The results obtained from Tafel polarization and EIS indicated the improved corrosion behavior of the welded specimen NZ with a decrease in the heat input during the welding process unlike the copper and brass metals.Furthermore,an increased heat input during the welding process shows a reduction in the conditions for forming the passive films with higher protection behavior.
文摘The processing of sintered brass products is described. The effect of processing parameters on the mechanical properties of the products is discussed. The relationship between the main mechanical properties and the friction and wear characteristics is analyzed. The tribological behaviour of the material is determined under different conditions (speed, load, time, environment etc). Comparison is made with that of dense products. The friction and wearmechanisms are investigated. Results are instructive to the application of the material.