Poly （vinyl butyral） （PVB） hollow fiber membranes were fabricated via thermally induced phase separation （TIPS）. The effects of coagulation bath temperature （CBT） on the structure and performance of membranes ...Poly （vinyl butyral） （PVB） hollow fiber membranes were fabricated via thermally induced phase separation （TIPS）. The effects of coagulation bath temperature （CBT） on the structure and performance of membranes were investigated in detail. The morphologies of the membranes were studied by scanning electron microscopy （SEM）, the performances of water permeability, rejection, breaking strength and elongation were measured, respectively. The results indicate that all the membranes have the asymmetric morphology and the thickness of the skin layer decreases and the pore size of the outer layer increases with the increase of CBT. The permeability of membranes prepared at air gap 1.0 cm and take-up speed 0.253 m/s increases from 1.047×10-7 to 5.909×10-7 m3/（m2·s-kPa） with the CBT increasing from 20 ℃ to 40℃, and sharply increases to 35.226×10 7 m3/（m2.s.kPa）once the CBT arrives at 50 ℃. While the carbonic ink rejections have no significant decrease, totally exceed 98%, but that of acid-maleic acid copolymer greatly decreases with the increase of CBT. Both the breaking strength and elongation decrease with the increase of CBT.展开更多
In this Study,Cadmium Oxide(CdO)nanostructures were synthesized by using Chemical Bath Deposition Technique.The synthesized process was carried out at room temperature.The structural and optical properties of nanostru...In this Study,Cadmium Oxide(CdO)nanostructures were synthesized by using Chemical Bath Deposition Technique.The synthesized process was carried out at room temperature.The structural and optical properties of nanostructures was characterized by XRD,SEM and UV-Vis techniques.As a result,the CdO nanostructures are oriented along(111)plane of cubic crystal structure.The morphology of CdO nanostructures showed interconnected prism-like and cauliflower-type cluster nanostructure.The UV results of this structures with high absorbtion coefficient are observed to be in accordance with the CdO nanoparticles.展开更多
There are lots of residual nickel and organic compounds in the spent electroless nickel plating bath. It not only wastes resource but also causes environmental pollution if the wastewater is discharged without treatme...There are lots of residual nickel and organic compounds in the spent electroless nickel plating bath. It not only wastes resource but also causes environmental pollution if the wastewater is discharged without treatment. In this paper, electrolytic method and reduction method for treating spent electroless nickel plating bath were compared. The factors studied included reaction time, pH, temperature, effectiveness and cost. It was found that the recovery rate of nickel by reduction was 99.9% under the condition ofpH 6, 50℃ for 10 min. The purity of reclaimed nickel was 66.1%. This treatment needed about 16 g NaBH4 for a liter spent solution, which cost RMB 64 Yuan. For electrolysis method, with pH 7.6, 80℃, 0.45 A （current intensity） for 2 h, the recovery rate reached 97.3%. The purity was 88.5% for the reclaimed nickel. Moreover, it was found that through electrolysis, the value of TOC （Total Organic Carbon） decreased from 114 to 3.08 g·L^-1 with removal rate of 97.3%. The main cost of electrolysis came from electric energy. It cost about 0.09 kWh （less than RMB 0.1 Yuan） per liter wastewater. Compared with reduction, electrolysis had more advantages, so the priority of selection should be given to the electrolysis method for the treatment of spent electroless nickel plating bath.展开更多
基金Project(21176264)supported by the National Natural Science Foundation of ChinaProject(11JJ2010)supported by the Hunan Provincial Natural Science Foundation of China
文摘Poly （vinyl butyral） （PVB） hollow fiber membranes were fabricated via thermally induced phase separation （TIPS）. The effects of coagulation bath temperature （CBT） on the structure and performance of membranes were investigated in detail. The morphologies of the membranes were studied by scanning electron microscopy （SEM）, the performances of water permeability, rejection, breaking strength and elongation were measured, respectively. The results indicate that all the membranes have the asymmetric morphology and the thickness of the skin layer decreases and the pore size of the outer layer increases with the increase of CBT. The permeability of membranes prepared at air gap 1.0 cm and take-up speed 0.253 m/s increases from 1.047×10-7 to 5.909×10-7 m3/（m2·s-kPa） with the CBT increasing from 20 ℃ to 40℃, and sharply increases to 35.226×10 7 m3/（m2.s.kPa）once the CBT arrives at 50 ℃. While the carbonic ink rejections have no significant decrease, totally exceed 98%, but that of acid-maleic acid copolymer greatly decreases with the increase of CBT. Both the breaking strength and elongation decrease with the increase of CBT.
文摘In this Study,Cadmium Oxide(CdO)nanostructures were synthesized by using Chemical Bath Deposition Technique.The synthesized process was carried out at room temperature.The structural and optical properties of nanostructures was characterized by XRD,SEM and UV-Vis techniques.As a result,the CdO nanostructures are oriented along(111)plane of cubic crystal structure.The morphology of CdO nanostructures showed interconnected prism-like and cauliflower-type cluster nanostructure.The UV results of this structures with high absorbtion coefficient are observed to be in accordance with the CdO nanoparticles.
基金Supported by National Natural Science Foundation of China (59870469)Homecoming Foundation of Heilongjiang Province (LC06C04)Researcher Overseas Foundation of the Department of Education of Heilongjiang Province (1152hq19)
文摘There are lots of residual nickel and organic compounds in the spent electroless nickel plating bath. It not only wastes resource but also causes environmental pollution if the wastewater is discharged without treatment. In this paper, electrolytic method and reduction method for treating spent electroless nickel plating bath were compared. The factors studied included reaction time, pH, temperature, effectiveness and cost. It was found that the recovery rate of nickel by reduction was 99.9% under the condition ofpH 6, 50℃ for 10 min. The purity of reclaimed nickel was 66.1%. This treatment needed about 16 g NaBH4 for a liter spent solution, which cost RMB 64 Yuan. For electrolysis method, with pH 7.6, 80℃, 0.45 A （current intensity） for 2 h, the recovery rate reached 97.3%. The purity was 88.5% for the reclaimed nickel. Moreover, it was found that through electrolysis, the value of TOC （Total Organic Carbon） decreased from 114 to 3.08 g·L^-1 with removal rate of 97.3%. The main cost of electrolysis came from electric energy. It cost about 0.09 kWh （less than RMB 0.1 Yuan） per liter wastewater. Compared with reduction, electrolysis had more advantages, so the priority of selection should be given to the electrolysis method for the treatment of spent electroless nickel plating bath.