In the present study,the mechanical properties of polyvinyl alcohol(PVA)-basalt hybrid fiber reinforced engineered cementitious composites(ECC)after exposure to elevated temperatures were experimentally investigated.F...In the present study,the mechanical properties of polyvinyl alcohol(PVA)-basalt hybrid fiber reinforced engineered cementitious composites(ECC)after exposure to elevated temperatures were experimentally investigated.Five temperatures of 20,50,100,200 and 400℃ were set to evaluate the residual compressive,tensile and flexural behaviors of hybrid and mono fiber ECC.It was shown that partial replacement of PVA fibers with basalt fibers endowed ECC with improved residual compressive toughness,compared to brittle failure of mono fiber ECC heated to 400℃.The tension tests indicated that the presence of basalt fibers benefited the tensile strength up to 200℃,and delayed the sharp reduction of strength to 400℃.Under flexural load,the peak deflections corresponding to flexural strengths of hybrid fiber ECC were found to be less vulnerable ranging from 20 to 100℃.Further,the scanning electron microscopy(SEM)results uncovered that the rupture of basalt fiber at moderate temperature and its pullout mechanism at high temperature was responsible for the mechanical evolution of hybrid fiber ECC.This work develops a better understanding of elevated temperature and basalt fiber impact on the residual mechanical properties and further provides guideline for tailoring ECC for improved fire resistance.展开更多
The recent increase in blast/bombing incidents all over the world has pushed the development of effective strengthening approaches to enhance the blast resistance of existing civil infrastructures.Engineered geopolyme...The recent increase in blast/bombing incidents all over the world has pushed the development of effective strengthening approaches to enhance the blast resistance of existing civil infrastructures.Engineered geopolymer composite(EGC)is a promising material featured by eco-friendly,fast-setting and strain-hardening characteristics for emergent strengthening and construction.However,the fiber optimization for preparing EGC and its protective effect on structural elements under blast scenarios are uncertain.In this study,laboratory tests were firstly conducted to evaluate the effects of fiber types on the properties of EGC in terms of workability,dry shrinkage,and mechanical properties in compression,tension and flexure.The experimental results showed that EGC containing PE fiber exhibited suitable workability,acceptable dry shrinkage and superior mechanical properties compared with other types of fibers.After that,a series of field tests were carried out to evaluate the effectiveness of EGC retrofitting layer on the enhancement of blast performance of typical elements.The tests include autoclaved aerated concrete(AAC)masonry walls subjected to vented gas explosion,reinforced AAC panels subjected to TNT explosion and plain concrete slabs subjected to contact explosion.It was found that EGC could effectively enhance the blast resistance of structural elements in different scenarios.For AAC masonry walls and panels,with the existence of EGC,the integrity of specimens could be maintained,and their deflections and damage were significantly reduced.For plain concrete slabs,the EGC overlay could reduce the diameter and depth of the crater and spallation of specimens.展开更多
Kang et al.published a research article on the treatment of ischemic stroke using engineered Treg cells(Kang et al.,Prog Biochem Biophys,2025,52(4):946-956.DOI:10.16476/j.pibb.2025.0019).Their study mainly explores th...Kang et al.published a research article on the treatment of ischemic stroke using engineered Treg cells(Kang et al.,Prog Biochem Biophys,2025,52(4):946-956.DOI:10.16476/j.pibb.2025.0019).Their study mainly explores the immunoregulatory role of regulatory T(Treg)cells in ischemic stroke,providing an innovative therapeutic strategy.Neuroinflammation is a major driver of secondary injury after stroke.Existing treatments focus on vascular recanalization while neglecting immune regulation.Their study proposes to modulate neuroinflammation through in vitro-induced Treg cells,offering a novel approach distinct from traditional thrombolysis and endovascular interventions.展开更多
Simple cubic black phosphorus(BP)has been recognized as a strategic material due to its exceptional structural stability under extreme conditions.In this investigation,simple cubic BP was successfully synthesized thro...Simple cubic black phosphorus(BP)has been recognized as a strategic material due to its exceptional structural stability under extreme conditions.In this investigation,simple cubic BP was successfully synthesized through shock-induced phase transformation,utilizing amorphous red phosphorus as the precursor material.The phase evolution process was systematically investigated using plane shock loading apparatus,with shock pressure and temperature parameters being precisely controlled to optimize transformation kinetics.Comprehensive phase characterization revealed the correlation between thermodynamic loading profiles and cubic BP formation efficiency.Precursor modification strategies were implemented through orthorhombic BP utilization,resulting in enhanced cubic phase yield and crystallinity.The synthesized cubic BP variants are considered promising candidates for advanced protective material systems,particularly where combinations of mechanical resilience and thermal stability are required under extreme operational conditions.This research provides critical insights into shock-induced phase transformation mechanics,while establishing foundational protocols for manufacturing non-equilibrium materials with potential applications in next-generation defensive technologies.展开更多
基金Project(51808545)supported by the National Natural Science Foundation of ChinaProject(8184083)supported by the Beijing Natural Science Foundation,ChinaProject(2021YQLJ05)supported by the Fundamental Research Funds for the Central Universities,China。
文摘In the present study,the mechanical properties of polyvinyl alcohol(PVA)-basalt hybrid fiber reinforced engineered cementitious composites(ECC)after exposure to elevated temperatures were experimentally investigated.Five temperatures of 20,50,100,200 and 400℃ were set to evaluate the residual compressive,tensile and flexural behaviors of hybrid and mono fiber ECC.It was shown that partial replacement of PVA fibers with basalt fibers endowed ECC with improved residual compressive toughness,compared to brittle failure of mono fiber ECC heated to 400℃.The tension tests indicated that the presence of basalt fibers benefited the tensile strength up to 200℃,and delayed the sharp reduction of strength to 400℃.Under flexural load,the peak deflections corresponding to flexural strengths of hybrid fiber ECC were found to be less vulnerable ranging from 20 to 100℃.Further,the scanning electron microscopy(SEM)results uncovered that the rupture of basalt fiber at moderate temperature and its pullout mechanism at high temperature was responsible for the mechanical evolution of hybrid fiber ECC.This work develops a better understanding of elevated temperature and basalt fiber impact on the residual mechanical properties and further provides guideline for tailoring ECC for improved fire resistance.
基金National Natural Science Foundation of China(Grant Nos.51908188 and 51938011).
文摘The recent increase in blast/bombing incidents all over the world has pushed the development of effective strengthening approaches to enhance the blast resistance of existing civil infrastructures.Engineered geopolymer composite(EGC)is a promising material featured by eco-friendly,fast-setting and strain-hardening characteristics for emergent strengthening and construction.However,the fiber optimization for preparing EGC and its protective effect on structural elements under blast scenarios are uncertain.In this study,laboratory tests were firstly conducted to evaluate the effects of fiber types on the properties of EGC in terms of workability,dry shrinkage,and mechanical properties in compression,tension and flexure.The experimental results showed that EGC containing PE fiber exhibited suitable workability,acceptable dry shrinkage and superior mechanical properties compared with other types of fibers.After that,a series of field tests were carried out to evaluate the effectiveness of EGC retrofitting layer on the enhancement of blast performance of typical elements.The tests include autoclaved aerated concrete(AAC)masonry walls subjected to vented gas explosion,reinforced AAC panels subjected to TNT explosion and plain concrete slabs subjected to contact explosion.It was found that EGC could effectively enhance the blast resistance of structural elements in different scenarios.For AAC masonry walls and panels,with the existence of EGC,the integrity of specimens could be maintained,and their deflections and damage were significantly reduced.For plain concrete slabs,the EGC overlay could reduce the diameter and depth of the crater and spallation of specimens.
文摘Kang et al.published a research article on the treatment of ischemic stroke using engineered Treg cells(Kang et al.,Prog Biochem Biophys,2025,52(4):946-956.DOI:10.16476/j.pibb.2025.0019).Their study mainly explores the immunoregulatory role of regulatory T(Treg)cells in ischemic stroke,providing an innovative therapeutic strategy.Neuroinflammation is a major driver of secondary injury after stroke.Existing treatments focus on vascular recanalization while neglecting immune regulation.Their study proposes to modulate neuroinflammation through in vitro-induced Treg cells,offering a novel approach distinct from traditional thrombolysis and endovascular interventions.
基金supported by the Youth Project of the Independent Subject of the State Key Laboratory of Explosion Science and Safety Protection,Beijing Institute of Technology(Grant Nos.QNKT25-13 and QNKT24-02)the 76th batch of Project funded by China Postdoctoral Science Foundation(Grant No.2024M764116)+3 种基金the National Natural Science Foundation of China(Grant Nos.12002048,12072037,12102050,and 12202067)the Science and Technology Commission,China(Grant No.2019-jcjc-zd-011-00)the Project supported by the Open Funds of Kui Yuan Laboratory(Grant No.KY202431)the State Key Laboratory of Explosion Science and Safety Protection(Grant No.KFJJ25-21M)。
文摘Simple cubic black phosphorus(BP)has been recognized as a strategic material due to its exceptional structural stability under extreme conditions.In this investigation,simple cubic BP was successfully synthesized through shock-induced phase transformation,utilizing amorphous red phosphorus as the precursor material.The phase evolution process was systematically investigated using plane shock loading apparatus,with shock pressure and temperature parameters being precisely controlled to optimize transformation kinetics.Comprehensive phase characterization revealed the correlation between thermodynamic loading profiles and cubic BP formation efficiency.Precursor modification strategies were implemented through orthorhombic BP utilization,resulting in enhanced cubic phase yield and crystallinity.The synthesized cubic BP variants are considered promising candidates for advanced protective material systems,particularly where combinations of mechanical resilience and thermal stability are required under extreme operational conditions.This research provides critical insights into shock-induced phase transformation mechanics,while establishing foundational protocols for manufacturing non-equilibrium materials with potential applications in next-generation defensive technologies.