A novel aliphatic sulfonie acid ion exchange resin was prepared from ethylenediamined polystyrene(PS-acyl-EDA),2-acrylamido-2-methylproanesulfonic acid(AMPS)by Michael reaction.This kind of resin has a longer chain th...A novel aliphatic sulfonie acid ion exchange resin was prepared from ethylenediamined polystyrene(PS-acyl-EDA),2-acrylamido-2-methylproanesulfonic acid(AMPS)by Michael reaction.This kind of resin has a longer chain than conventional sulphonic polystyrene resin,that is,the former is easier to react with other compound.The effect of the reaction time,reaction temperature,catalyst amount,reagent amount and the charge ration on reaction result were discussed.Under the optimum condition,the maximum loading of the sulfonie acid ion exchange resin could be up to 1.15 mmol·g-1 resin.The product was characterized with FT-IR.The filling material of chromatographic column could be prepared by this method.展开更多
以2-丙烯酰胺-2-甲基丙磺酸(AMPS)为单体、CuCl/N,N,N′,N′-四甲基乙二胺(TMEDA)为催化体系,氯乙酰化聚苯乙烯微球(PS-acyl-Cl)为大分子引发剂,经原子转移自由基聚合反应(ATRP),于微球表面接枝聚脂肪族磺酸(PAMPS)链段获得脂肪族磺酸...以2-丙烯酰胺-2-甲基丙磺酸(AMPS)为单体、CuCl/N,N,N′,N′-四甲基乙二胺(TMEDA)为催化体系,氯乙酰化聚苯乙烯微球(PS-acyl-Cl)为大分子引发剂,经原子转移自由基聚合反应(ATRP),于微球表面接枝聚脂肪族磺酸(PAMPS)链段获得脂肪族磺酸基强酸性阳离子交换树脂(PS-g-PAMPS)。考察了反应温度、溶剂体系、pH值、催化剂、反应时间等条件对接枝反应的影响,在优化的反应条件下,使用氯乙酰基担载量为3.82 mmol g 1的PS-acyl-Cl,10 h可获得担载量为1.99 mmol g 1的PS-g-PAMPS。产物经过红外,元素分析表征。该PS-g-PAMPS较传统的磺酸基树脂有较长的手臂长度,位阻小,易于和其它物质反应,TG分析显示具有很好的热稳定性。展开更多
以湖南株洲污染土壤作为研究对象,研究了Na-EDTA、NH_4-EDTA、Ca-EDTA在不同浓度下对土壤中Cd的去除效果,确定出适合的浓度与淋洗剂;并采用氯型717阴离子交换树脂对土壤淋洗液中的EDTA-Cd络合物进行吸附与回收试验,主要方法流程如下:采...以湖南株洲污染土壤作为研究对象,研究了Na-EDTA、NH_4-EDTA、Ca-EDTA在不同浓度下对土壤中Cd的去除效果,确定出适合的浓度与淋洗剂;并采用氯型717阴离子交换树脂对土壤淋洗液中的EDTA-Cd络合物进行吸附与回收试验,主要方法流程如下:采用静态法考察了固液比、pH值、时间、温度对树脂吸附EDTA-Cd络合物的影响,确定最佳吸附条件;采用上柱吸附法研究了在不同流速下穿透曲线的变化,确定树脂的穿透点;选取Fe_2(SO_4)_3多价金属盐溶液作为再生剂,对树脂中的EDTA-Cd络合物进行动态洗脱回收,测定出洗脱曲线与体积.随后进行连续5次吸附洗脱试验,探究树脂的再生性与树脂中EDTA-Cd络合物的回收效果.结果表明,在浓度为2.5 mmol·L^(-1)时,Na-EDTA、NH_4-EDTA、Ca-EDTA溶液对土壤中的Cd具有较好的去除效果,其去除率分别为64.75%、66.11%、68.29%.另外,在静态吸附过程中,随着固液比增加,树脂对EDTACd的吸附效率减少,在pH值为5.6时,对EDTA-Cd络合物吸附效率达到93.53%,树脂达到吸附平衡所需的时间为30—45 min,最佳反应温度区间为25—35℃;在动态吸附回收过程中,当上柱流速为4 m L·min^(-1)时,树脂达穿透点所需EDTA-Cd络合溶液为650 m L;再生剂Fe_2(SO_4)_3的洗脱体积为60 m L,洗脱溶液与吸附EDTA-Cd络合物溶液的体积比例达到1∶10.经过连续5次吸附洗脱试验后,树脂对EDTA-Cd络合物的去除率和再生率分别达到76.64%—93.43%、75.65%—84.19%.利用氯型717阴离子交换树脂提取以及回收土壤淋洗液中EDTA-Cd络合物是可行的.展开更多
文摘A novel aliphatic sulfonie acid ion exchange resin was prepared from ethylenediamined polystyrene(PS-acyl-EDA),2-acrylamido-2-methylproanesulfonic acid(AMPS)by Michael reaction.This kind of resin has a longer chain than conventional sulphonic polystyrene resin,that is,the former is easier to react with other compound.The effect of the reaction time,reaction temperature,catalyst amount,reagent amount and the charge ration on reaction result were discussed.Under the optimum condition,the maximum loading of the sulfonie acid ion exchange resin could be up to 1.15 mmol·g-1 resin.The product was characterized with FT-IR.The filling material of chromatographic column could be prepared by this method.
文摘用一个阴离子树脂交换性能微柱连续测定系统(MCCD),在动态条件下考察影响大孔型强碱阴离子树脂性能的各种因素,得到了测定其交换容量的最佳参数:柱长度为60 mm,内径3.0 mm;树脂层高度40 mm,填充量为0.1720 g;再生剂NaOH浓度3%,流速0.6 m l/m in,再生剂耗量为433 m l/g(树脂);样品水为20 mg/L酸性氯离子溶液,流速1.3 m l/m in。在最佳参数下,对各种大孔型强碱阴离子树脂、凝胶型树脂、均粒与非均粒树脂的交换性能进行了测定和对比;MCCD法与国标法的相关系数为r=0.990,它具有试剂耗量少、操作简单、自动化程度高等优点,通过一次测定,可同时给出树脂的工作交换容量、平衡交换容量、全交换容量、交换速率、利用率等多个参数。
文摘以2-丙烯酰胺-2-甲基丙磺酸(AMPS)为单体、CuCl/N,N,N′,N′-四甲基乙二胺(TMEDA)为催化体系,氯乙酰化聚苯乙烯微球(PS-acyl-Cl)为大分子引发剂,经原子转移自由基聚合反应(ATRP),于微球表面接枝聚脂肪族磺酸(PAMPS)链段获得脂肪族磺酸基强酸性阳离子交换树脂(PS-g-PAMPS)。考察了反应温度、溶剂体系、pH值、催化剂、反应时间等条件对接枝反应的影响,在优化的反应条件下,使用氯乙酰基担载量为3.82 mmol g 1的PS-acyl-Cl,10 h可获得担载量为1.99 mmol g 1的PS-g-PAMPS。产物经过红外,元素分析表征。该PS-g-PAMPS较传统的磺酸基树脂有较长的手臂长度,位阻小,易于和其它物质反应,TG分析显示具有很好的热稳定性。
文摘以湖南株洲污染土壤作为研究对象,研究了Na-EDTA、NH_4-EDTA、Ca-EDTA在不同浓度下对土壤中Cd的去除效果,确定出适合的浓度与淋洗剂;并采用氯型717阴离子交换树脂对土壤淋洗液中的EDTA-Cd络合物进行吸附与回收试验,主要方法流程如下:采用静态法考察了固液比、pH值、时间、温度对树脂吸附EDTA-Cd络合物的影响,确定最佳吸附条件;采用上柱吸附法研究了在不同流速下穿透曲线的变化,确定树脂的穿透点;选取Fe_2(SO_4)_3多价金属盐溶液作为再生剂,对树脂中的EDTA-Cd络合物进行动态洗脱回收,测定出洗脱曲线与体积.随后进行连续5次吸附洗脱试验,探究树脂的再生性与树脂中EDTA-Cd络合物的回收效果.结果表明,在浓度为2.5 mmol·L^(-1)时,Na-EDTA、NH_4-EDTA、Ca-EDTA溶液对土壤中的Cd具有较好的去除效果,其去除率分别为64.75%、66.11%、68.29%.另外,在静态吸附过程中,随着固液比增加,树脂对EDTACd的吸附效率减少,在pH值为5.6时,对EDTA-Cd络合物吸附效率达到93.53%,树脂达到吸附平衡所需的时间为30—45 min,最佳反应温度区间为25—35℃;在动态吸附回收过程中,当上柱流速为4 m L·min^(-1)时,树脂达穿透点所需EDTA-Cd络合溶液为650 m L;再生剂Fe_2(SO_4)_3的洗脱体积为60 m L,洗脱溶液与吸附EDTA-Cd络合物溶液的体积比例达到1∶10.经过连续5次吸附洗脱试验后,树脂对EDTA-Cd络合物的去除率和再生率分别达到76.64%—93.43%、75.65%—84.19%.利用氯型717阴离子交换树脂提取以及回收土壤淋洗液中EDTA-Cd络合物是可行的.