The effect of sinter basicity on softening-melting behaviors of mixed burden made from chromium-bearing vanadium-titanium magnetite(Cr-V-Ti magnetite) was investigated and the function mechanism was simultaneously ana...The effect of sinter basicity on softening-melting behaviors of mixed burden made from chromium-bearing vanadium-titanium magnetite(Cr-V-Ti magnetite) was investigated and the function mechanism was simultaneously analyzed.The results show that with increasing sinter basicity from 1.71 to 2.36,the softening interval tends to increase from 149.3 ℃ to 181.7 ℃while the melting interval tends to decrease from 178.0 ℃ to 136.7 ℃.The location of cohesive zone moves downwards firstly and then ascends slightly,but the cohesive zone becomes thinner.The softening-melting characteristic value becomes small,which indicates that the permeability of burden column is improved.The dripping ratio of mixed burden tends to increase firstly and then decrease,which comes to the highest value of 74.50%when the sinter basicity is 2.13.The content and the recovery of V and Cr in dripping iron are all increased.The generation amount of components with high melting point in slag becomes little with the increase of sinter basicity,which could improve the permeability of mixed burden.Taking softening-melting behaviors of mixed burden and recovery of valuable elements into account,the proper sinter basicity is no less than 2.13 for smelting mixed burden made from Cr-V-Ti magnetite in blast furnace.展开更多
The thermal decomposition process of basic magnesium carbonate was investigated. Firstly, Basic magnesium carbonate was prepared from magnesite, and the characteristics of the product were detected by X-ray diffracti...The thermal decomposition process of basic magnesium carbonate was investigated. Firstly, Basic magnesium carbonate was prepared from magnesite, and the characteristics of the product were detected by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. Subsequently, the thermal decomposition process of basic magnesium carbonate in air was studied by thermogravimetry-differential thermogravimetry （TG-DTG）. The results of XRD confirm that the chemical composition of basic magnesium carbonate is 4MgCO3·Mg（OH）2·4H2O. And the SEM images show that the sample is in sheet structure, with a diameter of 0.1-1 μm. The TG-DTG results demonstrate that there are two steps in the thermal decomposition process of basic magnesium carbonate. The apparent activation energies （E） were calculated by Flyrm-Wall-Ozawa method. It is obtained from Coats-Redfem＇s equation and Malek method that the mechanism functions of the two decomposition stages are D3 and A1.5, respectively. And then, the kinetic equations of the two steps were deduced as well.展开更多
基金Project(51574067)supported by the National Natural Science Fundation of ChinaProjects(2012AA062302,2012AA062304)supported by the National High Technology Research and Development Program of ChinaProject(N110202001)supported by the Fundamental Research Funds for the Central Universities of China
文摘The effect of sinter basicity on softening-melting behaviors of mixed burden made from chromium-bearing vanadium-titanium magnetite(Cr-V-Ti magnetite) was investigated and the function mechanism was simultaneously analyzed.The results show that with increasing sinter basicity from 1.71 to 2.36,the softening interval tends to increase from 149.3 ℃ to 181.7 ℃while the melting interval tends to decrease from 178.0 ℃ to 136.7 ℃.The location of cohesive zone moves downwards firstly and then ascends slightly,but the cohesive zone becomes thinner.The softening-melting characteristic value becomes small,which indicates that the permeability of burden column is improved.The dripping ratio of mixed burden tends to increase firstly and then decrease,which comes to the highest value of 74.50%when the sinter basicity is 2.13.The content and the recovery of V and Cr in dripping iron are all increased.The generation amount of components with high melting point in slag becomes little with the increase of sinter basicity,which could improve the permeability of mixed burden.Taking softening-melting behaviors of mixed burden and recovery of valuable elements into account,the proper sinter basicity is no less than 2.13 for smelting mixed burden made from Cr-V-Ti magnetite in blast furnace.
基金Project(20876160) supported by the National Natural Science Foundation of China
文摘The thermal decomposition process of basic magnesium carbonate was investigated. Firstly, Basic magnesium carbonate was prepared from magnesite, and the characteristics of the product were detected by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. Subsequently, the thermal decomposition process of basic magnesium carbonate in air was studied by thermogravimetry-differential thermogravimetry （TG-DTG）. The results of XRD confirm that the chemical composition of basic magnesium carbonate is 4MgCO3·Mg（OH）2·4H2O. And the SEM images show that the sample is in sheet structure, with a diameter of 0.1-1 μm. The TG-DTG results demonstrate that there are two steps in the thermal decomposition process of basic magnesium carbonate. The apparent activation energies （E） were calculated by Flyrm-Wall-Ozawa method. It is obtained from Coats-Redfem＇s equation and Malek method that the mechanism functions of the two decomposition stages are D3 and A1.5, respectively. And then, the kinetic equations of the two steps were deduced as well.