Mesoporous CeO2 was first synthesized by hydrothermal method,and then used to synthesize different contents of CuO)x/CeO2(x:molar ratio of Cu to Ce) by deposition-precipitation method.These materials were characterize...Mesoporous CeO2 was first synthesized by hydrothermal method,and then used to synthesize different contents of CuO)x/CeO2(x:molar ratio of Cu to Ce) by deposition-precipitation method.These materials were characterized by X-ray diffraction(XRD),N2 adsorption and desorption,H2 temperature programmed reduction(H2-TPR) and O2 temperature programmed desorption(O2-TPD) to study the crystal structure,surface area,and the mechanism of CO oxidation.The results show that,on XRD patterns,no evidence of CuO diffraction peaks is present until Cu loading is increased to 20%.The BET surface area decreases noticeably with the increase of Cu content.Compared with other samples,the better reducibility and activity oxygen species of(CuO)10%/CeO2coincide with its better catalytic activity.展开更多
基金Project(2011FZ030)supported by the Natural Science Foundation of Yunnan Province,ChinaProjects(2011144,2011221)supported by Analysis and Test Foundation of Kunming University of Science and Technology,China
文摘Mesoporous CeO2 was first synthesized by hydrothermal method,and then used to synthesize different contents of CuO)x/CeO2(x:molar ratio of Cu to Ce) by deposition-precipitation method.These materials were characterized by X-ray diffraction(XRD),N2 adsorption and desorption,H2 temperature programmed reduction(H2-TPR) and O2 temperature programmed desorption(O2-TPD) to study the crystal structure,surface area,and the mechanism of CO oxidation.The results show that,on XRD patterns,no evidence of CuO diffraction peaks is present until Cu loading is increased to 20%.The BET surface area decreases noticeably with the increase of Cu content.Compared with other samples,the better reducibility and activity oxygen species of(CuO)10%/CeO2coincide with its better catalytic activity.