Nano-SiO2 was modified using silane coupling agent （KH-550） and hyperbranched poly（amine-ester） respectively, and Poly（vinyl chloride） （PVC）/modified nano-SiO2 composites were made by melt-blending. The compos...Nano-SiO2 was modified using silane coupling agent （KH-550） and hyperbranched poly（amine-ester） respectively, and Poly（vinyl chloride） （PVC）/modified nano-SiO2 composites were made by melt-blending. The composites＇ structures andmechanical properties were characterized by transmission electron microscopy（TEM）, sanning electronic microscopy（SEM） and electronic universal testing machine. The results. show that nano-SiO2 grafted by hyperbranched poly （amine-ester） increases obviously in dispersion in PVC matrix, and mechanical properties of PVC are effectively improved. Moreover, it was found that mechanical properties of PVC/nano-SiO2 composites reach the best when weight percent of nano-SiO2 in PVC matrix is 1%. Compared with crude PVC, the tensile strength of hyperbranched poly （amine-ester） grafted nano-SiO2/ PVC composite increases by 24.68 % and its break elongation, flexural strength and impact strength increase by 15.73%, 4.07% and 1 841.84%, respectively. Moreover, the processing of the composites is improved.展开更多
A new method of surface chemical modification of nano-SiO2 is proposed in this paper. In the presence of catalyst, the active hydroxyl groups on the surface of nano-SiO2 reacted with AB2-type monomer （N, N-dihydroxye...A new method of surface chemical modification of nano-SiO2 is proposed in this paper. In the presence of catalyst, the active hydroxyl groups on the surface of nano-SiO2 reacted with AB2-type monomer （N, N-dihydroxyethyl-3-amino methyl propionate） by one-step polycondensation. And the product＇s Fourer transform infrared （FTIR） graphs and transmission electron microscopy（TEM） images proved that hyperbranched poly （amine-ester） was grafted on nano-SiO2 surface successfully. Results show that the modified nano-SiO2 exhibits excellent dispersion and stability in some solvents such as alcohol and chloroform.展开更多
基金Sponsored by the Ministerial Level Advanced Research Foundation (120701BQ0126)
文摘Nano-SiO2 was modified using silane coupling agent （KH-550） and hyperbranched poly（amine-ester） respectively, and Poly（vinyl chloride） （PVC）/modified nano-SiO2 composites were made by melt-blending. The composites＇ structures andmechanical properties were characterized by transmission electron microscopy（TEM）, sanning electronic microscopy（SEM） and electronic universal testing machine. The results. show that nano-SiO2 grafted by hyperbranched poly （amine-ester） increases obviously in dispersion in PVC matrix, and mechanical properties of PVC are effectively improved. Moreover, it was found that mechanical properties of PVC/nano-SiO2 composites reach the best when weight percent of nano-SiO2 in PVC matrix is 1%. Compared with crude PVC, the tensile strength of hyperbranched poly （amine-ester） grafted nano-SiO2/ PVC composite increases by 24.68 % and its break elongation, flexural strength and impact strength increase by 15.73%, 4.07% and 1 841.84%, respectively. Moreover, the processing of the composites is improved.
基金Sponsored by the Ministerial Level Advanced Research Foundation (120701BQ0126)
文摘A new method of surface chemical modification of nano-SiO2 is proposed in this paper. In the presence of catalyst, the active hydroxyl groups on the surface of nano-SiO2 reacted with AB2-type monomer （N, N-dihydroxyethyl-3-amino methyl propionate） by one-step polycondensation. And the product＇s Fourer transform infrared （FTIR） graphs and transmission electron microscopy（TEM） images proved that hyperbranched poly （amine-ester） was grafted on nano-SiO2 surface successfully. Results show that the modified nano-SiO2 exhibits excellent dispersion and stability in some solvents such as alcohol and chloroform.