The effects of Yb/Zr micro-alloying on the microstructure,mechanical properties,and corrosion resistance of an Al-Zn-Mg-Cu alloy were systematically investigated.Upon the addition of Yb/Zr to the Al-Zn-Mg-Cu alloy,the...The effects of Yb/Zr micro-alloying on the microstructure,mechanical properties,and corrosion resistance of an Al-Zn-Mg-Cu alloy were systematically investigated.Upon the addition of Yb/Zr to the Al-Zn-Mg-Cu alloy,the grain boundaries were pinned by high-density nanosized Al_(3)(Yb,Zr)precipitates during extrusion deformation,consequently,the average grain size was significantly reduced from 232.7μm to 3.2μm.This grain refinement contributed substantially to the improvement in both strength and elongation.The ultimate tensile strength,yield strength,and elongation of the Yb/Zr modified alloy increased to 705.3 MPa,677.6 MPa,and 8.7%,respectively,representing enhancements of 16.2%,19.3%,and 112.2%compared to the unmodified alloy.Moreover,the distribution of MgZn_(2)phases along grain boundaries became more discontinuous in the Yb/Zr modified alloy,which effectively retarded the propagation of intergranular corrosion and improved the corrosion resistance.展开更多
The asymmetric creep aging behaviors of a pre-treated Al-Zn-Mg-Cu alloy under high and low stresses have been investigated for high precision creep age forming application of aluminum integral panels.With the increase...The asymmetric creep aging behaviors of a pre-treated Al-Zn-Mg-Cu alloy under high and low stresses have been investigated for high precision creep age forming application of aluminum integral panels.With the increase of applied stress,the creep strains under the tensile stresses are higher than those of compressive stresses and the asymmetry of creep strain is more obvious.However,the mechanical properties of tensile stress creep aged samples are lower than those of compressive stress creep aged samples.Dislocation density,dislocation moving velocity and the proportion of precipitates directly lead to the asymmetry of creep strain and mechanical properties after tensile-compressive creep aging process.In addition,the tensile and compressive stresses have little effect on the width of the precipitate-free zone(PFZ).It indicates that in the high stress creep age forming process of the pretreated Al-Zn-Mg-Cu alloy,the tensile stress promotes the dislocation motion to obtain a better creep strain but weakens its mechanical properties compared with the compressive stress.In the field of civil aviation aircraft component manufacturing,the introduction of tension and compression stress asymmetry into the creep constitutive model may improve the accuracy of creep age forming components.展开更多
基金Project(51501228)supported by the National Natural Science Foundation of ChinaProject(202109)supported by the Open Sharing Fund for the Large-scale Instruments and Equipments of Central South University,China。
文摘The effects of Yb/Zr micro-alloying on the microstructure,mechanical properties,and corrosion resistance of an Al-Zn-Mg-Cu alloy were systematically investigated.Upon the addition of Yb/Zr to the Al-Zn-Mg-Cu alloy,the grain boundaries were pinned by high-density nanosized Al_(3)(Yb,Zr)precipitates during extrusion deformation,consequently,the average grain size was significantly reduced from 232.7μm to 3.2μm.This grain refinement contributed substantially to the improvement in both strength and elongation.The ultimate tensile strength,yield strength,and elongation of the Yb/Zr modified alloy increased to 705.3 MPa,677.6 MPa,and 8.7%,respectively,representing enhancements of 16.2%,19.3%,and 112.2%compared to the unmodified alloy.Moreover,the distribution of MgZn_(2)phases along grain boundaries became more discontinuous in the Yb/Zr modified alloy,which effectively retarded the propagation of intergranular corrosion and improved the corrosion resistance.
基金Project(2021YFB3400900)supported by the National Key R&D Program of ChinaProjects(51905551,52205435)supported by the National Natural Science Foundation of China Youth Foundation+1 种基金Project(2022ZZTS0196)supported by the Fundamental Research Founds for the Central Universities,ChinaProject(CX20220282)supported by the Hunan Provincial Innovation Foundation for Postgraduate,China。
文摘The asymmetric creep aging behaviors of a pre-treated Al-Zn-Mg-Cu alloy under high and low stresses have been investigated for high precision creep age forming application of aluminum integral panels.With the increase of applied stress,the creep strains under the tensile stresses are higher than those of compressive stresses and the asymmetry of creep strain is more obvious.However,the mechanical properties of tensile stress creep aged samples are lower than those of compressive stress creep aged samples.Dislocation density,dislocation moving velocity and the proportion of precipitates directly lead to the asymmetry of creep strain and mechanical properties after tensile-compressive creep aging process.In addition,the tensile and compressive stresses have little effect on the width of the precipitate-free zone(PFZ).It indicates that in the high stress creep age forming process of the pretreated Al-Zn-Mg-Cu alloy,the tensile stress promotes the dislocation motion to obtain a better creep strain but weakens its mechanical properties compared with the compressive stress.In the field of civil aviation aircraft component manufacturing,the introduction of tension and compression stress asymmetry into the creep constitutive model may improve the accuracy of creep age forming components.