High-purity silver(Ag)is extensively utilized in electronics,aerospace,and other advanced industries due to its excellent thermal conductivity,electrical conductivity,and machinability.However,the prohibitive material...High-purity silver(Ag)is extensively utilized in electronics,aerospace,and other advanced industries due to its excellent thermal conductivity,electrical conductivity,and machinability.However,the prohibitive material cost poses substantial challenges for optimizing thermal processing parameters through repetitive experimental trials.In this work,hot compression experiments on high-purity silver were conducted using a Gleeble-3800 thermal simulator.The high temperature deformation behaviors,dynamic recovery(DRV)and dynamic recrystallization(DRX)of high-purity silver were studied by constructing an Arrhenius constitutive equation and developing thermal processing maps.The results show that plastic instability of high-purity silver occurs at high strain rates and the optimized hot processing parameters are the strain rate below 0.001 s^(−1) and the temperature of 340−400℃.Microstructural observations exhibit that DRV prefers to occur at lower deformation temperatures(e.g.,250℃).This is attributed to the low stacking fault energy of high-purity silver,which facilitates the decomposition of dislocations into partial dislocations and promotes high-density dislocation accumulation.Furthermore,DRX in high-purity silver becomes increasingly pronounced with increasing deformation temperature and reaches saturation at 350℃.展开更多
The pronounced anisotropy in mechanical properties presents a major obstacle to the extensive application of aluminum-lithium(Al-Li)alloys,primarily attributed to heterogeneous precipitate distribution,grain structure...The pronounced anisotropy in mechanical properties presents a major obstacle to the extensive application of aluminum-lithium(Al-Li)alloys,primarily attributed to heterogeneous precipitate distribution,grain structure variations,and crystallographic texture.This study investigates the impact of pre-thermal treatment prior to hot rolling and aging treatment on the anisotropy of mechanical properties of 2195 alloy sheet fabricated by gas atomization,hot pressing and hot rolling.The results demonstrate that pre-treatment at 450℃for 4 h promotes finer and more uniform distribution of precipitates,effectively mitigating mechanical anisotropy of the alloy sheet.Additionally,this treatment facilitates recrystallization during hot rolling,further reducing mechanical anisotropy.The in-plane anisotropy(IPA)factors for ultimate tensile strength(UTS)and yield strength(YS)are 1.15%and 0.77%,respectively.Subsequent aging treatment enhances grain refinement and the uniformity of the T_(1) phase,suppresses the formation of precipitation-free zones(PFZs),significantly improving the strength and toughness of the alloy sheet.After peak aging at 165℃for 48 h,the alloy sheet exhibits YS of 547 MPa,UTS of 590 MPa,and elongation(EL)of 7.7%.展开更多
基金Project(52274369)supported by the National Natural Science Foundation of China。
文摘High-purity silver(Ag)is extensively utilized in electronics,aerospace,and other advanced industries due to its excellent thermal conductivity,electrical conductivity,and machinability.However,the prohibitive material cost poses substantial challenges for optimizing thermal processing parameters through repetitive experimental trials.In this work,hot compression experiments on high-purity silver were conducted using a Gleeble-3800 thermal simulator.The high temperature deformation behaviors,dynamic recovery(DRV)and dynamic recrystallization(DRX)of high-purity silver were studied by constructing an Arrhenius constitutive equation and developing thermal processing maps.The results show that plastic instability of high-purity silver occurs at high strain rates and the optimized hot processing parameters are the strain rate below 0.001 s^(−1) and the temperature of 340−400℃.Microstructural observations exhibit that DRV prefers to occur at lower deformation temperatures(e.g.,250℃).This is attributed to the low stacking fault energy of high-purity silver,which facilitates the decomposition of dislocations into partial dislocations and promotes high-density dislocation accumulation.Furthermore,DRX in high-purity silver becomes increasingly pronounced with increasing deformation temperature and reaches saturation at 350℃.
基金Project(52274369)supported by the National Natural Science Foundation of ChinaProject(623020034)supported by the National Key Laboratory of Science and Technology on High-strength Structural Materials,China。
文摘The pronounced anisotropy in mechanical properties presents a major obstacle to the extensive application of aluminum-lithium(Al-Li)alloys,primarily attributed to heterogeneous precipitate distribution,grain structure variations,and crystallographic texture.This study investigates the impact of pre-thermal treatment prior to hot rolling and aging treatment on the anisotropy of mechanical properties of 2195 alloy sheet fabricated by gas atomization,hot pressing and hot rolling.The results demonstrate that pre-treatment at 450℃for 4 h promotes finer and more uniform distribution of precipitates,effectively mitigating mechanical anisotropy of the alloy sheet.Additionally,this treatment facilitates recrystallization during hot rolling,further reducing mechanical anisotropy.The in-plane anisotropy(IPA)factors for ultimate tensile strength(UTS)and yield strength(YS)are 1.15%and 0.77%,respectively.Subsequent aging treatment enhances grain refinement and the uniformity of the T_(1) phase,suppresses the formation of precipitation-free zones(PFZs),significantly improving the strength and toughness of the alloy sheet.After peak aging at 165℃for 48 h,the alloy sheet exhibits YS of 547 MPa,UTS of 590 MPa,and elongation(EL)of 7.7%.