摘要
Aluminum sheets were polished to reduce ruggedness and then textured in varying acid-ethanol concentration etchant to form pores. The textured surface was characterized structurally by using X-ray diffraction (XRD) which revealed aluminum crystallographic planes (1 1 1), (2 0 0), (2 2 0) and (3 1 1). Its morphology was studied by using energy dispersive X-ray (EDX) and scanning electron microscope (SEM) that confirmed purity of aluminum sheet to be 99.66% at. Reflectance of textured and plain aluminum sheet was analyzed by spectrophotometric measurements which showed that texturing reduced the reflectance of the polished surface by 26% in the UV-VIS-NIR spectrum of solar radiation. With reduced reflectance of the textured aluminum sheet, it was applicable for solar radiation absorption.
Aluminum sheets were polished to reduce ruggedness and then textured in varying acid-ethanol concentration etchant to form pores. The textured surface was characterized structurally by using X-ray diffraction (XRD) which revealed aluminum crystallographic planes (1 1 1), (2 0 0), (2 2 0) and (3 1 1). Its morphology was studied by using energy dispersive X-ray (EDX) and scanning electron microscope (SEM) that confirmed purity of aluminum sheet to be 99.66% at. Reflectance of textured and plain aluminum sheet was analyzed by spectrophotometric measurements which showed that texturing reduced the reflectance of the polished surface by 26% in the UV-VIS-NIR spectrum of solar radiation. With reduced reflectance of the textured aluminum sheet, it was applicable for solar radiation absorption.