自由体积与亲水性对环氧涂层防护性能的影响 被引量:12

Effect of Free Volume and Water Affinity on Corrosion Protection of Epoxy Resin Coatings
在线阅读 下载PDF
导出
摘要 报道了涂层聚合物自由体积和亲水性对涂层腐蚀防护性能影响的初步研究结果.实验表明,相对于自由体积,树脂的亲水性是决定树脂吸水率的更主要因素.低亲水性涂层腐蚀防护性能的提高主要源自到达涂层/金属界面的水量的显著降低.但由于采用活性酯固化的环氧树脂涂层中水通道的尺寸相对较大,水合离子扩散较容易,因此该类涂层覆盖下的金属基体被润湿部分的腐蚀趋势反而较一般涂层为大. The effect of free volume and water affinity of coating polymers on the corrosion protection of epoxy resin coatings was evaluated using a series of epoxy resin coatings obtained by curing o-cresol novolac epoxy resin with mixed hardener comprising novolac resin (NOV) and novolac acetate resin (NOVA) in different molar ratios. It was found that, as the molar content of NOVA increased, the room- temperature density of the cured resins decreased with increase in free volume and decrease in water affinity. The results of the water sorption of the resins suggested that water affinity is more important than free volume in determining water sorption of the coatings. While the water sorption of the coating decreased linearly with the decrease of water affinity of the coating, the corrosion protection of the coatings increased much more significantly. The great improvement in corrosion protection of the coating with less water affinity can be mainly attributed to the less amount of water that reaches the coating/metal interface as demonstrated by electrochemical impedance spectroscopic measurement. However, owing to the larger diameter of the water passages in the NOVA cured epoxy resin matrix, diffusion of hydrated ion to the polymer/coating interface is easier which resulted in an increase of the concentration of corrosive ions in the interfacial region, and therefore, the corrosion tendency of the metal substrate at the wetted places under the coating is larger than that of general coating.
出处 《物理化学学报》 SCIE CAS CSCD 北大核心 2004年第4期360-363,共4页 Acta Physico-Chimica Sinica
基金 国家自然科学基金(20375023)资助项目~~
关键词 自由体积 亲水性 环氧树脂涂层 防护性能 金属腐蚀 电化学阻抗谱 epoxy resin free volume water affinity water sorption corrosion protection
  • 相关文献

参考文献20

  • 1Zhang, S. Y.; Luo, X. W.; Li, S. J.; Zhou, W. F. Chemistry,1997,8:31[张树永,罗小雯,李善君,周伟舫.化学通报( Huaxue Tongbao) , 1997, 8:31 ]
  • 2Armstrong, R. D.; Wright, J. D.; Handyside, T. M. J. Appl.Electrochem., 1992, 22:795
  • 3Mansfeld, F.; Tsai, C. H. Corros., 1991, 47:958
  • 4van Westing, E. P. M.; Ferrari, G. M.; de Wit, J. H. W.Electrochim. Acta, 1994, 39:899
  • 5Bonora, P. L.; Deflorian, F.; Fedrizzi, L. Mater. Sci. Forum,1995, 192:267
  • 6van Westing, E. P. M.; Ferrari, G. M.; de Wit, J. H. W.Corros. Sci., 1994, 36:1323
  • 7van Westing, E. P. M.; Ferrari, G. M.; de Wit, J. H. W.Corros. Sci., 1993, 34:1511
  • 8Zhang, S. Y.; Ding, Y. F.; Li, S. J.; Luo, X. W.; Zhou, W. F.Corros. Sci., 2002, 44:861
  • 9Lee, M. C.; Peppas, N. A. Prog. Polym. Sci., 1993, 18:947
  • 10Suzuki, T.; Oki, Y.; Numajiri, M.; Miura, T.; Kondo, K.; Shiomi,Y.; Ito, Y. Polym., 1996, 37:3025

二级参考文献7

共引文献10

同被引文献139

引证文献12

二级引证文献73

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部