摘要
用NaF、NaCl、H3BO3和Na2HPO4作矿化剂,灼烧温度为1350℃和1400℃,改变Sm3+掺杂量,制备出黄色颜料SmxCe(1-x-0.04)Mo0.04O(2-x/2+δ)(x=0.1~0.5),用CIE颜色系统—L*a*b*(1976)色空间体系和紫外可见反射光谱分析其呈色性能,结果表明:当Sm3+掺杂量x=0.3时,在灼烧温度1350℃以H3BO3为矿化剂和在灼烧温度1400℃以NaCl为矿化剂时,分别得到呈色鲜艳的亮黄色颜料。
The yellow pigments of SmxCe(1-x-0.04)Mo0.04O(2-x/2+δ)(x=0.1-0.5) were prepared by adding the mineralizers as Na F, Na Cl, H3BO3 and Na2HPO4 and the calcination temperature at 1350 ℃ and 1400 ℃ and changing doping amounts of Sm3+. the chromatic performance were analysted by the CIE 1976 L*a*b* colorimetric scales and UV-vis reflectance spectroscopy. The results show that the brilliant yellow pigments were prepared respectively that the doping content of Sm3+ was x=0.3 when the mineralizer was H3BO3 at 1350 ℃ and the mineralizer was Na Cl at 1400 ℃.