摘要
针对高地应力存在岩爆风险隧洞的防护需求,通过优化矿物掺合料配比与钢纤维掺量,复配10%早强剂开发超高性能喷射混凝土(UHPFRCC)。结果表明:该体系净浆流动度达303 mm,仅需4%速凝剂即可达到常规喷射混凝土中净浆凝结时间;其3h抗压强度(11.5 MPa)和8 h弯曲韧性指数I_(20)(26.8)分别为常规喷射混凝土的360%和250%,且在8h龄期实现抗压强度为26.4 MPa与超高韧性I_(20)为26.8,为深埋隧洞强岩爆防治提供关键材料解决方案。
In response to the protection needs of tunnels with high ground stress and rockburst risk,this study developed ultra-high performance shotcrete(UHPFRC)by optimizing the ratio of mineral admixture and the amount of steel fiber,and compounding 10%early strength agent.The results showed that:The net slurry flow of the system reaches 303mm,and only 4%accelerator is needed to achieve the setting time of the net slurry in conventional shotcrete;its 3-hour compressive strength and 8-hour bending toughness index I20 are 360%and 250%of conventional shotcrete respectively,and the compressive strength is 26.4MPa and ultra-high toughness I20 is 26.8 at the 8-hour age,providing key material solutions for the prevention and control of strong rock burst in deeply buried tunnels.
作者
马勇
陈涛
雷英强
马俊峰
闫涛
程凯歌
MA Yong;CHEN Tao;LEI Yingqiang;Ma Junfeng;YAN Tao;CHENG Kaige(Sinohydro Bureau 7 Co.,Ltd.,Chengdu 611730,China)
出处
《四川水力发电》
2025年第S2期164-168,共5页
Sichuan Hydropower
基金
中国水利水电第七工程局有限公司科技项目(SDQJ-ZDZX-2023-1-19)
中国电力建设股份有限公司科技项目(DJ-ZDZX-2019-01-10)。
关键词
高地应力
岩爆
超早强高韧性喷射混凝土
配合比
抗折强度
抗压强度
high ground stress
rockburst
ultra-early and high-toughness shotcrete
mix ratio
flexural strength
compressive strength