采用熔炼法制备了等原子比的铁钴镍铜铂、铁钴镍铜钯、铁钴镍铜钌三种高熵合金块体材料,通过X射线衍射测试发现三种材料均为面心立方结构。经电化学测试发现:铁钴镍铜铂高熵合金材料在析氢反应过程中具有低至152.8mV的过电位,展现出优秀的电解水析氢催化活性;铁钴镍铜铂高熵合金材料在析氧反应过程中具有低至68.8mV/dec的塔菲尔斜率,展现出优秀的电解水析氧催化效率。铁钴镍铜铂高熵合金材料只包含20%原子含量的贵金属铂,且制备方法成熟,具有材料成本优势,因而铁钴镍铜铂在工业电解水制氢方面具有良好的应用潜力。
Three equiatomic high-entropy alloy(HEA)bulk materials—FeCoNiCuPt,FeCoNiCuPd,and FeCoNiCuRu were prepared us-ing a melting method.X-ray diffraction analysis confirmed that all three materials exhibit a face-centered cubic structure.Electrochemical tests re-vealed the FeCoNiCuPt HEA demonstrates exceptional hydrogen evolution reaction catalytic activity with an overpotential as low as 152.8 mV;The FeCoNiCuPt HEA shows outstanding oxygen evolution reaction catalytic efficiency with a Tafel slope of only 68.8 mV/dec.Notably,the FeCoNiCuPt HEA contains only 20%platinum—a noble metal—and leverages mature synthesis techniques,granting it significant cost advantages.Consequently,FeCoNiCuPt exhibits promising potential for industrial hydrogen production via water splitting.
作者
袁铖
刘思慧
谢铭曦
丁亮
赵春旺
Yuan Cheng;Liu Sihui;Xie Mingxi;Ding Liang;Zhao Chunwang(School of Materials and Energy,Foshan University,Guangdong,528000)
出处
《当代化工研究》
2025年第12期32-34,共3页
Modern Chemical Research
基金
广东省普通高校创新团队项目(项目编号:2023KCXTD030)
佛山大学学生学术基金项目(项目编号:xsjj202406zrb06)。
关键词
高熵合金
催化剂
电解水
high-entropy alloys
catalysts
water splitting
作者简介
袁铖(2004-),男,汉族,广东韶关人,本科,研究方向:新能源材料与器件。;通信作者:赵春旺(1971-),男,汉族,内蒙古呼和浩特人,博士,教授,研究方向:材料物理与化学。E-mail:zhaocw@fosu.edu.cn。