本文研究了不同含水量对拉挤环氧/酸酐体系理化性能和固化性能的影响。通过旋转流变仪、差式扫描量热仪、万能试验机等测试手段,探究了树脂中不同含水量对环氧/酸酐体系的黏度变化、T_(g)和固化行为的影响,并对环氧树脂浇注体力学性能进行了分析。结果表明:随着环氧树脂体系内含水量的增加,环氧树脂的耐热性能逐渐下降,浇注体力学性能呈现降低的趋势;在含水树脂中添加适量甲基四氢苯酐,可有效降低水分对环氧/酸酐体系固化性能的影响。
In this paper,the effects of water content on the physical and chemical properties and curing properties of epoxy resin were studied.Through varions testing methods,such as rotating rotators,differential scanning heat meters,universal testing machine,the effect of different water content on the viscosity,Tg,curing behavior and mechanical properties of the epoxy resin system were explored.The results showed that as the water content in the epoxy resin system increased,the heat resistance of epoxy resin gradually decreased,and the mechanical performance of casting decreased.Adding modest doses of MTHPA to the aqueous resin can reduce the negative effect on the curing performance of the epoxy-anhydride system impact of water content.
作者
王朔
贾晨辉
杨智明
姚亚琳
WANG Shuo;JIA Chenhui;YANG Zhiming;YAO Yalin(Beijing FRP Institute Tengzhou Composites Materials Co.,Ltd.,Tengzhou 277500,China;Beijing Composite Materials Co.,Ltd.,Beijing 102101,China)
出处
《复合材料科学与工程》
北大核心
2025年第2期28-33,共6页
Composites Science and Engineering
基金
年产3万吨高性能碳纤维建设项目(50003023052)
北京玻钢院复合材料有限公司自立项目(50003023042)。
关键词
环氧/酸酐体系
含水量
固化行为
力学性能
复合材料
epoxy/anhydride system
water content
curing behavior
mechanical performance
composites
作者简介
第一作者:王朔(1992-),男,硕士研究生,助理工程师,主要从事酚醛、环氧树脂及复合材料方面的研究;通信作者:姚亚琳(1985-),男,硕士研究生,高级工程师,主要从事酚醛、环氧树脂及复合材料方面的研究,yaoyalin777@126.com;通信作者:杨智明(1986-),男,硕士研究生,工程师,主要从事高分子复合材料方面的研究,372065527@qq.com。