摘要
采用FeCl3作为催化剂的氧化偶联聚合法合成了具有交联活性的聚3-(4-叠氮基苯甲氧基乙基)噻吩(P3AET)。用核磁共振、红外光谱、凝胶液相色谱、热重分析、差示扫描量热法、紫外-可见光光谱和循环伏安法表征了聚合物的结构、热稳定性能、交联特性和光电性能。结果表明,P3AET的氯仿溶液的紫外吸收区域为340 nm^550 nm,最大吸收峰在420 nm左右处,聚合物热交联温度约为170℃,电化学禁带宽度约为1.96 eV。P3AET有望作为聚合物太阳能给体材料。
Cross-linkable poly( 3-( 4-azido-benzoyloxy ethyl) thiophene)( P3AET) was synthesized by oxidative coupling polymerization,using FeCl3as catalyst. The structure,thermal stability,cross-link property and photoelectronic performance of P3AET were characterized by1H-NMR,FT-IR,GPC,TGA,DSC,UV-Vis absorption and cyclic voltammetry measurements. The results show that the absorption onsets range from 340 nm to 573 nm in chloroform solution with an absorption peak at 420 nm. The thermal crosslink temperature is 170 ℃ and the electrochemistry bandgap of P3AET is about 1. 96 eV. As a result,P3AET can be promising donor unit for polymer solar cells.
出处
《高分子材料科学与工程》
EI
CAS
CSCD
北大核心
2014年第6期10-13,共4页
Polymer Materials Science & Engineering
基金
国家自然科学基金资助项目(60976019)
教育部高等学校博士学科点专项科研基金(20093223110002)
福建省引进高层次创业创新人才
“闽江学者”特聘教授(闽教高[2010]79号)
高校科技创新团队等支持计划(闽教科[2012]03号)
福建省教育厅科技项目(JA12069)