A copper-red and silver-white metallic glaze of R_(2)O-RO-Al_(2)O_(3)-SiO_(2)-P_(2)O_(5)system was synthesized by adjusting the firing temperature and glaze components.The coloration mechanism of the metallic glaze was revealed via investigation of the microstructure of the glaze.Our research reveals that the metallic glaze with different colors is mainly due to the amount of Fe_(2)O_(3).The metallic glaze shows a silver-white luster due to a structural color ofα-Fe_(2)O_(3)crystals with a good orientation when the sample contains 0.0939 mol of Fe_(2)O_(3),maintaining temperatures at 1150℃for 0.5 h.The metallic glaze is copper-red which is dominated by the coupling of chemical and structural color ofα-Fe_(2)O_(3)crystals when the sample contains 0.0783 mol of Fe_(2)O_(3).After testing the amount of SiO_(2),we find that 4.0499 mol is the optimal amount to form the ceramic network,and 0.27 mol AlPO_(4)is the best amount to promote phase separation.
基金
Funded by the National Natural Science Foundation of China(No.52202231)
the College Students Innovation and Entrepreneurship Training Program of Hubei University of Technology(No.202310500039)。
作者简介
CHEN Yanlin:Prof.,E-mail:chenyl70@126.com;Corresponding author:WANG Juan:E-mail:jwang@hbut.edu.cn。