摘要
The Zn0.6Cu wires are fabricated into stents for the potential biodegradable application of nasal wound healing.The degradation behavior of Zn0.6Cu stents in 0.9 wt%NaCl at 36.5℃ is evaluated.It shows that the untreated Zn0.6Cu stent experiences severe crevice corrosion with acceleration and autocatalytic effects within the micro-cracks and ruptures at 4.67±1.15 d,with the average corrosion rate of 0.28 mm y^(-1).Fortunately,the anodic polarization(AP)+hydrothermal(H)conversion coating,consisting of ZnCO_(3),Zn(OH)_(2) and ZnO,could inhibit the crevice corrosion significantly by reducing the cathode/anode ratio,extending the rupture time up to 16.50±2.95 d,with the average corrosion rate of 0.14 mm y^(-1).This research indicates that the biodegradable Zn-based stent has some potential applications in nasal wound recovery area.