摘要
通过Gleeble-3800试验机,开展了C630R转子钢在温度1000~1200℃、应变速率0.01~1 s^(-1)条件下的热压缩试验,研究了热变形行为及不同工艺参数对其显微组织的影响,计算了C630R转子钢的本构方程,并绘制了真应变为0.8时的热加工图。结果表明,C630R转子钢的流变应力随变形温度升高和应变速率减小而降低;随着变形温度升至1200℃,或者应变速率降至0.01 s^(-1),C630R转子钢更倾向于产生动态再结晶。利用修正的流变应力曲线,计算出C630R转子钢的热变形激活能Q为530.155 kJ/mol,本构方程为·ε=5.85×1018[sinh(0.0114σ)]4.852·exp(-530155/RT),绘制了真应变为0.8时的热加工图。结合显微组织,C630R转子钢在真应变0.8时合理的热加工工艺参数为变形温度1075~1200℃,应变速率0.01~0.11 s^(-1)。
Thermal compression test of C630R rotor steel was carried out by Gleeble-3800 thermal simulation testing machine at temperature range of 1000-1200℃and strain rate of 0.01-1 s^(-1),the thermal deformation behavior and the influence of different process parameters on the microstructure were studied,the constitutive equation and hot processing map of the C630R rotor steel at true strain of 0.8 was constructed.The experimental results indicate that the true stress of the C630R rotor steel decreases with the enhancement of deformation temperatures to 1200℃and the reduction of true strain rate to 0.01 s^(-1).When the deformation temperature is higher and the compression strain rate is lower,C630R rotor steel is preferred to produce dynamic recrystallization.Thermal deformation activation energy Q of the C630R rotor steel is calculated to be 530.155 kJ/mol by using the corrected flow stress curves,and the constitutive equation is·ε=5.85×1018[sinh(0.0114σ)]4.852·exp(-530155/RT),the processing maps at true strain of 0.8 are plotted.The reasonable thermal processing parameters for C630R rotor steel under true strain of 0.8 is:deformation temperature of 1075-1200℃,strain rate of 0.01-0.11 s^(-1).
作者
邱佳佳
何西扣
唐正焮
霍洁
Qiu Jiajia;He Xikou;Tang Zhengxin;Huo Jie(Research Institute of Special Steels,Central Iron and Steel Research Institute Co.,Ltd.,Beijing 100081,China;Tianjin Heavy Industries Research&Development Co.,Ltd.,CFHI,Tianjin 300457,China)
出处
《特殊钢》
2024年第3期56-61,共6页
Special Steel
基金
国家重点研发计划项目(2021YFB3704100,2021YFB3704101)
钢铁研究总院自主投入研发专项基金(事21T62610B)。
关键词
C630R转子钢
变形温度
应变速率
本构方程
热加工图
C630R Rotor Steel
Deformation Temperatures
Strain Rate
Constitutive Equation
Hot Processing Map
作者简介
邱佳佳(1994—),男,博士,E-mail:qiujiajia1994@126.com;通信作者:何西扣(1985—),男,博士,正高级工程师,E-mail:he_xikou@163.com。