摘要
采用共沉淀方法合成了一种新型氟化物红色荧光粉BaTaF_(7)∶Mn^(4+),确定了BaTaF_(7)的组成与晶体结构,研究并讨论了晶体结构与发光性能之间的关系。在紫外(UV)和蓝光激发下,BaTaF_(7)∶Mn^(4+)荧光粉在630 nm表现出强烈的零声子线(ZPL)发射,其源于晶体结构中[MnF_(7)]畸变八面体的C3v群对称环境。由YAG∶Ce3+和BaTaF_(7)∶Mn^(4+)荧光粉混合制备的暖白光LED表现出较优异的性能,表明BaTaF_(7)∶Mn^(4+)具有成为暖白色发光二极管红色荧光粉的应用潜力。
A novel red fluoride phosphor BaTaF_(7)∶Mn^(4+)was synthesized via the conventional co-precipitation method.The structure and luminescence properties of BaTaF_(7)∶Mn^(4+)were investigated and discussed under various conditions.The BaTaF_(7)∶Mn^(4+)phosphor shows strong ZPL emission intensity at about 630 nm under ultraviolet(UV)and blue light excitation.It originated from the highly distorted Mn^(4+)octahedral coordination environment in the C3v group symmetry.A warm LED fabricated with a blend of YAG∶Ce3+and the BaTaF_(7)∶Mn^(4+)phosphor showed excellent performance,indicating BaTaF_(7)∶Mn^(4+)potential for application as a red phosphor for warm WLEDs.
作者
孔俊人
周洋
张世瑞
李蕊芯
王晓明
焦桓
KONG Junren;ZHOU Yang;ZHANG Shirui;LI Ruixin;WANG Xiaoming;JIAO Huan(School of Chemistry&Chemical Engineering,Shaanxi Normal University,Xi'an 710119,China)
出处
《发光学报》
EI
CAS
CSCD
北大核心
2023年第6期975-984,共10页
Chinese Journal of Luminescence
基金
国家自然科学基金(51972203,22271180)。
作者简介
孔俊人(2000-),女,河南汝州人,硕士研究生,2022年于河南科技大学获得学士学位,主要从事无机发光材料的研究。E-mail:1783075920@qq.com;王晓明(1983-),男,内蒙古鄂尔多斯人,博士,副教授,2012年于北京大学获得博士学位,主要从事无机固体功能材料、氮化物发光材料与离子导体材料的研究。E-mail:xmwang@snnu.edu.cn;焦桓(1968-),女,陕西三原人,博士,教授,2001年于西北工业大学获得博士学位,主要从事固体无机材料、照明显示发光材料与新能源材料的基础与应用的研究。E-mail:jiaohuan@snnu.edu.cn。