摘要
目的在聚丙烯(PP)五层共挤出软管的外层中引入一定质量分数环烯烃共聚物(COC)材料,研究其对软管阻隔性能的影响。方法将不同质量分数的COC与PP共混造粒,对共混物进行熔融行为分析,并测试软管的阻氧与阻水性能,共混材料的拉伸强度、弯曲模量、缺口冲击强度等。结果随着COC添加量的增加,软管管身的氧气透过速率与水蒸气透过速率降低。当COC质量分数为20%时,氧气透过率低至3.3 cm^(3)/(d·m^(2)),水蒸气透过率为0.6 g/(d·m^(2)),此时其他性能也能实现较好的平衡。结论在PP五层共挤出软管的外层中引入COC可以有效地提升软管阻水与阻氧性能。
The work aims to introduce a certain proportion of cyclic olefin copolymer(COC)material into the outer layer of polypropylene(PP)five-layer co-extrusion hoses,and study its effect on the barrier performance of the hoses.The melting behavior of the COC/PP blends of different proportions was analyzed.The oxygen and water resistance properties,tensile strength,bending modulus,notched impact strength of the blends were also tested.With the increase of COC,the permeability of oxygen and water vapor decreased.When the COC dosage was 20 wt%,the oxygen permeability was as low as 3.3 cm^(3)/(d·m^(2)),and the water vapor permeability was 0.6 g/(d·m^(2)).At the meantime,the other properties also achieved a good balance.It is concluded that the presence of COC can effectively improve the water and oxygen resistance performance of the PP five-layer co-extrusion hoses.
作者
熊治雨
熊伟
林茂青
李虹
林新华
王鑫
关平
彭晓华
XIONG Zhi-yu;XIONG Wei;LIN Mao-qing;LI Hong;LIN Xin-hua;WANG Xin;GUAN Ping;PENG Xiao-hua(Shenzhen Leaguer Co.,Ltd.,Guangdong Shenzhen 518057,China;School of Materials Science and Engineering,South China University of Technology,Guangzhou 510641,China;Shenzhen 863 New Material Technology Co.,Ltd.,Guangdong Shenzhen 518117,China)
出处
《包装工程》
CAS
北大核心
2023年第5期51-56,共6页
Packaging Engineering
关键词
环烯烃共聚物
聚丙烯
五层共挤出软管
阻隔性
cyclic olefin copolymer
polypropylene
five layers of co-extruded hose
barrier
作者简介
熊治雨(1989—),男,博士后,高级工程师,主要研究方向为高阻隔膜材料。