摘要
Hollow ternary metal oxides have shown enormous potential in lithium-ion batteries(LIBs),which is ascribed to their complex chemical composition,abundant active defect sites,and the synergy effect be-tween metals.In this work,we synthesized Mo-doped NiCo_(2)O_(4) porous spheres with yolk-shell structure by using a simple self-templating method.Surprisingly,other than the yolk-shell structure we had ob-tained,the inner core of the yolk-shell was also porous,which could fully enhance the electrolyte infil-tration and promote the transmission of lithium ions(Li+)and electrons(e−).The diameter of the porous core in the yolk-shell sphere was about 530 nm,and the outer shell’s thickness was up to 110 nm.In addition,the unique pores in the core appeared in the diameter of about 85 nm.With this structure,the volume expansion of the anode could be well inhibited during charge/discharge.It exhibited prominent electrochemical performance with high reversible capacity(1338 mA h g^(−1) at 100 mA g^(−1)),satisfactory cycle life(1360 mA h g^(−1) after 200 cycles at 100 mA g^(−1)),and exceptional rate capability(820 mA h g^(−1) at 2000 mA g^(−1))as anode material in LIBs.
基金
financially supported by the National Natural Science Foundation of China (Nos. 51972180, 51572134 and 41907315)
the Key Technology Research and Development Program of Shandong (No. 2019GGX102070)
the Program for Scientific Research Innovation Team in Colleges and Universities of Jinan (No. 2018GXRC006)。
作者简介
Corresponding authors:Yinan Wang.E-mail addresses:wangyn@qlu.edu.cn;Corresponding authors:Guowei Zhou.E-mail addresses:gwzhou@qlu.edu.cn。