摘要
对某特钢企业250mm×280mm大方坯的振动频率、振幅、负滑脱时间等参数进行了优化试验,结果表明在拉速0.62~0.72m/min、负滑脱率NSR37%、振频137~147/min、负滑脱时间0.16~0.18s下生产的铸坯表面质量得到了明显提升,轧材黑皮表面探伤一次合格率由原58.6%提升至93.61%,减少了精整工序修磨量、生产效率也得到了明显提升。
By optimizing the parameters of vibration frequency, amplitude and negative slippage time of250mm × 280mm bloom in a special steel enterprise, the slab surface quality was improved obviously under the conditions of 0.62–0.72 m/min casting speed, NSR37% negative slippage rate, 137–147/min vibration frequency and 0.16 – 0.18 s negative slippage time. The qualified rate of black skin surface inspection was increased from58.6% to 93.61%, the grinding amount at finishing stage is reduced and the production efficiency is improved obviously.
作者
王海达
陈列
董贵文
李凯
王兴华
范世强
Wang HaiDa;Chenlie;Dong Guiwen;LiKai;Wang XingHua;Fan Shiqiang(Jianlong Beiman Special Steel Co.,Ltd.,Qiqihar 161041,Heilongjiang,China)
出处
《特钢技术》
CAS
2022年第1期15-18,共4页
Special Steel Technology
关键词
振动频率
振幅
负滑脱时间
结晶器振动
速度负滑脱率
vibration frequency
amplitude
negative slippage time
mold vibration
speed negative slippage rate