摘要
采用含有F、Cl、Br、I的苯肼小分子修饰石墨烯量子点(GQDs),制备了卤素功能化石墨烯量子点(X-GQDs)。通过较高电负性的卤族元素p型掺杂,提高了X-GQDs修饰的电极的功函数。将这种可溶液加工的X-GQDs用于聚合物太阳能电池的阳极界面层,与基于GQDs的器件的能量转换效率(PCE,9.01%)相比,基于X-GQDs的器件的PCE均得到了提高,基于F-GQDs的聚合物太阳能电池器件的PCE最高,达到11.75%。实验结果表明,基于X-GQDs的聚合物太阳能电池性能的提高是X-GQDs的高导电性与修饰后电极的高功函数共同作用的结果。因此,应用X-GQDs提高阳极功函数是一种制备高性能聚合物太阳能电池的方法。
The halogen-functionalized graphene quantum dots(X-GQDs,X represent F,Cl,Br,I)are prepared by function-alized GQDs with phenyl hydrazine molecules containing halogen elements.Halogen with high electronegativity can induce p-type doping in GQDs,which improve the work function of GQDs modified electrodes.The X-GQDs have been used as an anode interlayer in polymer solar cells.All the power conversion efficiency of X-GQDs based devices is higher than that of GQDs based devices(9.01%).The F-GQDs-based devices achieve the highest power conversion efficiency,11.75%.X-GQDs as anode interlayer materials are an efficient method to improve anode work function and to prepare high-performance polymer solar cells.
作者
葛晓美
苏振英
张坚
GE Xiaomei;SU Zhenying;ZHANG Jian(School of Material Science and Engineering,Guilin University of Electronic Technology,Guilin 541004,China;Guangxi Key Laboratory of Information Materials,Guilin University of Electronic Technology,Guilin 541004,China)
出处
《桂林电子科技大学学报》
2022年第1期80-86,共7页
Journal of Guilin University of Electronic Technology
基金
广西自然科学基金(2015GXNSFGA139002)。
作者简介
通信作者:张坚(1977-),男,教授,博士,研究方向为有机光电材料与器件。E-mail:Jianzhang@guet.edu.cn。